- 密度 [g/cm3]: 2.13
- 吸水率 [%]: 0.03
- 缺口冲击强度: 0.22
- 断裂伸长率 [%]: 89.9
- 弯曲强度 [MPa]: 53.5
- 弯曲模量 [MPa]: 19.03
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.13 g/cc | 0.0770 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 1.01 g/cc | 0.0365 lb/in³ | Apparent density per ASTM D1895 |
| Water Absorption | 0.030 % | 0.030 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00040 cm/cm | 0.00040 in/in | per ATM D955. Post shrinkage is 0.04% at 72hr 120ºC per ASTM D1299. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 88 | 88 | ASTM D785 |
| Tensile Strength, Ultimate | 53.5 MPa | 7760 psi | ASTM D638 |
| Tensile Modulus | 4.10 GPa | 595 ksi | ASTM D638 |
| Flexural Yield Strength | 89.9 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 19.03 GPa | 2760 ksi | ASTM D790 |
| Compressive Yield Strength | 183.3 MPa | 26590 psi | ASTM D695 |
| Izod Impact, Notched | 0.220 J/cm | 0.412 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.270 J/cm² | 1.28 ft-lb/in² | ASTM D256 |
| Impact | 44 | 44 | J/m Plenco drop ball test |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 6.89e+12 ohm-cm | 6.89e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.4 @Frequency 1e+6 Hz | 5.4 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 11.2 kV/mm | 284 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.019 @Frequency 1e+6 Hz | 0.019 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 190 sec | 190 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.940 W/m-K @Temperature 100 °C | 6.52 BTU-in/hr-ft²-°F @Temperature 212 °F | |
| Maximum Service Temperature, Air | 219 °C | 426 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 226 °C | 439 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.47 mm | V-0 @Thickness 0.0579 in | |
| Oxygen Index | 46 % | 46 % | ASTM D2863 |