- 密度 [g/cm3]: 1.51
- 吸水率 [%]: 0.24
- 缺口冲击强度: 0.23
- 断裂伸长率 [%]: 89.0
- 弯曲强度 [MPa]: 53.4
- 弯曲模量 [MPa]: 8.22
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.620 g/cc | 0.0224 lb/in³ | Apparent density per ASTM D1895 |
| Water Absorption | 0.24 % | 0.24 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | per ATM D955. Post shrinkage is 0.18% at 72hr 120ºC per ASTM D1299. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 89 | 89 | ASTM D785 |
| Tensile Strength, Ultimate | 53.4 MPa | 7750 psi | ASTM D638 |
| Elongation at Break | 1.01 % | 1.01 % | ASTM D638 |
| Tensile Modulus | 6.83 GPa | 991 ksi | ASTM D638 |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | ASTM D790 |
| Flexural Modulus | 8.22 GPa | 1190 ksi | ASTM D790 |
| Compressive Yield Strength | 206.2 MPa | 29910 psi | ASTM D695 |
| Izod Impact, Notched | 0.230 J/cm | 0.431 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.220 J/cm² | 1.05 ft-lb/in² | ASTM D256 |
| Impact | 130 | 130 | J/m Plenco drop ball test |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.44e+11 ohm-cm | 2.44e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.4 @Frequency 1e+6 Hz | 5.4 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 13.2 kV/mm | 335 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.045 @Frequency 1e+6 Hz | 0.045 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 80 sec | 80 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 58.0 µm/m-°C @Temperature 20.0 °C | 32.2 µin/in-°F @Temperature 68.0 °F | |
| Maximum Service Temperature, Air | 193 °C | 379 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |