- 拉伸强度 [MPa]: 62.1
- 弯曲模量 [MPa]: 20.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 | ||
| Volatiles | 2.0 - 4.0 % @Temperature 163 °C | 2.0 - 4.0 % @Temperature 325 °F | 10 min | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 75 | 75 | ASTM D2583 | ||
| Tensile Strength, Yield | 62.1 MPa @Temperature 23.9 °C | 9000 psi @Temperature 75.0 °F | 0° Direction, Dry; 325°F 2kpsi; ASTM D638 | ||
| Tensile Modulus | 26.2 GPa @Temperature 23.9 °C | 3800 ksi @Temperature 75.0 °F | 0° Direction, Dry; 325°F 2kpsi; ASTM D638 | ||
| Flexural Strength | 110 MPa @Temperature 23.9 °C | 16000 psi @Temperature 75.0 °F | Dry; 325°F 2kpsi; ASTM D790 | ||
| Flexural Modulus | 20.7 GPa @Temperature 23.9 °C | 3000 ksi @Temperature 75.0 °F | Dry; 325°F 2kpsi; ASTM D790 | ||
| Compressive Strength | 276 MPa @Temperature 23.9 °C | 40000 psi @Temperature 75.0 °F | Dry; 325°F 2kpsi; ASTM D695 | ||
| Compressive Modulus | 13.8 GPa @Temperature 23.9 °C | 2000 ksi @Temperature 75.0 °F | Dry; 325°F 2kpsi; ASTM D695 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 0.962 J/g-°C | 0.230 BTU/lb-°F | ASTM C351 | ||
| Thermal Conductivity | 3.89 W/m-K @Temperature 149 °C | 27.0 BTU-in/hr-ft²-°F @Temperature 300 °F | ASTM C177 | ||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 6.00 Month @Temperature 4.44 °C | 6.00 Month @Temperature 40.0 °F | |||
| Descriptive Properties | |||||
| Filler Content (%) | 2-4 | ||||
| Nominal Prepreg Weight (oz/yd) | 30 | ||||
| Resin Flow (%) | 7-17 | 325°F, 150psi | |||
| Resin Solids Content (%) | 30-36 | ||||