- 拉伸强度 [MPa]: 1550.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 | ||
| Volatiles | 3.0 - 5.0 % @Temperature 135 °C | 3.0 - 5.0 % @Temperature 275 °F | 8 min | ||
| Thickness | 254 microns | 10.0 mil | cured laminate, per ply | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 75 | 75 | ASTM D2583 | ||
| Tensile Strength, Yield | 1550 MPa @Temperature 23.9 °C | 225000 psi @Temperature 75.0 °F | 0° Direction, Dry; 325°F, 1000psi Cured; ASTM D638 | ||
| Tensile Modulus | 96.5 GPa @Temperature 23.9 °C | 14000 ksi @Temperature 75.0 °F | 0° Direction, Dry; 325°F, 1000psi Cured; ASTM D638 | ||
| Compressive Strength | 689 MPa @Temperature 23.9 °C | 100000 psi @Temperature 75.0 °F | Dry; 325°F, 1000psi Cured; ASTM D695 | ||
| Compressive Modulus | 96.5 GPa @Temperature 23.9 °C | 14000 ksi @Temperature 75.0 °F | Dry; 325°F, 1000psi Cured; ASTM D695 | ||
| Processing Properties | Metric | English | Comments | ||
| Gel Time | 0.800 - 3.30 min | 0.800 - 3.30 min | |||
| Shelf Life | 3.00 Month @Temperature 4.44 °C | 3.00 Month @Temperature 40.0 °F | |||
| 6.00 Month @Temperature -17.8 °C | 6.00 Month @Temperature 0.000 °F | ||||
| Descriptive Properties | |||||
| Fabric Area Weight (g/m²) | 300 | ||||
| Prepreg Resin Content (%) | 32-38 | ||||
| Resin Flow (%) | 5-20 | 325°F, 15psi | |||