- 密度 [g/cm3]: 1.14
- 缺口冲击强度: 1.6
- 弯曲强度 [MPa]: 22.0
- 弯曲模量 [MPa]: 1.03
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | Bayer Test |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | ASTM D638/D412 |
| Elongation at Break | 75 % | 75 % | ASTM D638/D412 |
| Flexural Modulus | 1.03 GPa | 149 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Tear Strength | 110 kN/m | 628 pli | Die C; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.4 µm/m-°C @Temperature 20.0 °C | 28.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |