- 密度 [g/cm3]: 1.25
- 缺口冲击强度: 1.7
- 弯曲强度 [MPa]: 28.0
- 弯曲模量 [MPa]: 1.44
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0059 cm/cm | 0.0059 in/in | Bayer Test |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM D638/D412 |
| Elongation at Break | 140 % | 140 % | ASTM D638/D412 |
| Flexural Modulus | 1.44 GPa | 209 ksi | ASTM D790 |
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| Tear Strength | 110 kN/m | 628 pli | Die C; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 52.0 µm/m-°C @Temperature 20.0 °C | 28.9 µin/in-°F @Temperature 68.0 °F | ASTM D696 |