| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.60 - 2.10 g/cc | 1.60 - 2.10 g/cc | ASTM D792 | ||
| 1.65 - 2.15 g/cc | 1.65 - 2.15 g/cc | Base Material; ASTM D792 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 65 | 65 | Base Material; ASTM D2240 | ||
| Tensile Strength at Break | >= 1.38 MPa | >= 200 psi | Base Material; ASTM D412 | ||
| 2.41 MPa | 350 psi | Reinforced Material - Fill; ASTM D412 | |||
| 4.48 MPa | 650 psi | Reinforced Material, warp; ASTM D412 | |||
| Elongation at Break | >= 50 % | >= 50 % | Reinforced Material - Fill/Warp; ASTM D412 | ||
| >= 100 % | >= 100 % | Base Material; ASTM D412 | |||
| Tear Strength | 5.25 kN/m | 30.0 pli | Base Material; ASTM D624 | ||
| 35.0 kN/m | 200 pli | Reinforced Material - Warp/Fill; ASTM D624 | |||
| Compression Set | 32 % | 32 % | 70 hrs @ 100°C; ASTM D395 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 0.0080 ohm-cm | 0.0080 ohm-cm | Reinforced Material; MIL-G-83528 | ||
| 0.0080 ohm-cm | 0.0080 ohm-cm | Base Material; MIL-G-83528 | |||
| <= 0.015 ohm-cm | <= 0.015 ohm-cm | Post Tensile Strength; MIL-G-83528 | |||
| Shielding Effectiveness | >= 60 dB | >= 60 dB | 200 kHz (H Field) - Base/Reinforced Material; MIL-G-83528 | ||
| >= 100 dB | >= 100 dB | 10 GHz (Plane Wave) - Base/Reinforced Material; MIL-G-83528 | |||
| >= 105 dB | >= 105 dB | 2 GHz (Plane Wave) - Base/Reinforced Material; MIL-G-83528 | |||
| >= 110 dB | >= 110 dB | 500 MHz (E Field) - Base/Reinforced Material; MIL-G-83528 | |||
| >= 115 dB | >= 115 dB | 100 MHz (E Field) - Base/Reinforced Material; MIL-G-83528 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 160 °C | 320 °F | |||
| Descriptive Properties | |||||
| Binder | Silicone, Base Material | ||||
| EMP Survivability kA / in, min | 0.9 | ||||
| Filler | Ag/Al, Reinforced Material | ||||
| Grade | Military-Aerospace | ||||
| Heat Aging - Base Material ohm-cm max | 0.01 | ||||
| Heat Aging - Reinforced Material ohm-cm max | 0.01 | ||||
| Low Temp Flex - Base Material, TR10 °C, min | -65 | ||||
| Low Temp Flex - Reinforced Material, TR10 °C, min | -65 | ||||
| Vibration Res, After - Base Material ohm-cm max | 0.008 | ||||
| 0.008 | |||||
| Vibration Res, During - Base Material ohm-cm max | 0.012 | ||||
| 0.012 | |||||