- 弯曲强度 [MPa]: 13.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 72 | 72 | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Elongation at Break | 345 % | 345 % | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| 100% Modulus | 0.00420 GPa | 0.609 ksi | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Compression Set | 58 % @Temperature 200 °C | 58 % @Temperature 392 °F | Method B, O-rings, 70 hr |