- 弯曲强度 [MPa]: 18.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 34 @Temperature 121 °C | 34 @Temperature 250 °F | ML-10 (gum)-Akron data |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 69 | 69 | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Tensile Strength, Ultimate | 18.2 MPa | 2640 psi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Elongation at Break | 186 % | 186 % | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Modulus of Elasticity | 0.000700 GPa | 0.102 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| 100% Modulus | 0.00670 GPa | 0.972 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Compression Set | 29 % @Temperature 200 °C | 29 % @Temperature 392 °F | Method B, O-rings 70 hr at 200°C (Post Cured 16 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | -30.8 °C | -23.4 °F | DSC, modulated |