- 弯曲强度 [MPa]: 18.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 51 @Temperature 121 °C | 51 @Temperature 250 °F | ML-10 (gum)-Akron data |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 67 | 67 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 18.2 MPa | 2640 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 298 % | 298 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.000800 GPa | 0.116 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00390 GPa | 0.566 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 20 % @Temperature 200 °C | 20 % @Temperature 392 °F | Method B, O-rings 70 hr at 200°C (Post Cured 2 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | -32.9 °C | -27.2 °F | DSC, modulated |