- 弯曲强度 [MPa]: 18.7
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 74 | 74 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 18.7 MPa | 2710 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 237 % | 237 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.00106 GPa | 0.154 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00660 GPa | 0.957 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 14 % @Temperature 200 °C | 14 % @Temperature 392 °F | Method B, O-rings 22 hr at 200°C (Post Cured 2 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | -5.40 °C | 22.3 °F | MDSC, postcured |