- 密度 [g/cm3]: 1.168
- 弯曲强度 [MPa]: 13.4
- 脆化温度 [℃]: -21.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.168 g/cc | 0.04220 lb/in³ | |
| Mooney Viscosity | 31 @Temperature 100 °C | 31 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 77 | 77 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 13.4 MPa | 1940 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 360 % | 360 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00550 GPa | 0.798 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.0103 GPa | 1.49 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.0128 GPa | 1.86 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 48.5 kN/m | 277 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 76 % @Temperature 125 °C | 76 % @Temperature 257 °F | Pellets cured MDR TC95 + 15 min at 160°C, 70 hr at 125°C; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -21.0 °C | -5.80 °F | Temperature Retraction, TR-10 |