- 密度 [g/cm3]: 0.94
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | |||
| Volatiles | 0.30 % @Treatment Temp. 105 °C, Time 3600 sec | 0.30 % @Treatment Temp. 221 °F, Time 1.00 hour | 5 g in hot air oven; ASTM D5668 | ||
| Mooney Viscosity | 55 @Temperature 100 °C | 55 @Temperature 212 °F | [MU] ML 1+4; ASTM D1646 | ||
| Ash | 0.30 % | 0.30 % | ASTM D5667 | ||
| Chemical Properties | Metric | English | Comments | ||
| Styrene Content | 25 % | 25 % | Bound; ASTM D5775 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 56.7 | 56.7 | ASTM D2240 | ||
| Tensile Strength at Break | 19.0 MPa @Treatment Temp. 145 °C, Time 2100 sec | 2760 psi @Treatment Temp. 293 °F, Time 0.583 hour | Cure; ASTM D412 | ||
| Elongation at Break | 510 % | 510 % | ASTM D412 | ||
| 300% Modulus | 0.0104 GPa | 1.51 ksi | ASTM D412 | ||
| Rebound | 18 % | 18 % | Resilience; ISO 4662 | ||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | -28.9 °C | -20.0 °F | HR 10 K/min, half height | ||
| Descriptive Properties | |||||
| Composition | 0.274 | Total Extractables; ASTM D5774 | |||
| 0.63 | Vinyl content | ||||
| Rheometer | 11.2 min | tc (50), ASTM D5289 | |||
| 15.0 dNm | MH, ASTM D5289 | ||||
| 18.4 min | tc (90), ASTM D5289 | ||||
| 3.1 dNm | ML, ASTM D5289 | ||||
| 7.8 min | ts2, test temperature 160°C; ASTM D5289 | ||||