- 弯曲强度 [MPa]: 14.0
- 脆化温度 [℃]: -5.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 15 @Temperature 100 °C | 15 @Temperature 212 °F | ML 1+4. Stock property.; ASTM D1646-81 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 82 | 82 | ASTM D2240-81 |
| Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D412-80 |
| Elongation at Break | 140 % | 140 % | ASTM D412-80 |
| 100% Modulus | 0.0124 GPa | 1.80 ksi | ASTM D412-80 |
| Tear Strength Test | 153 | 153 | lb-in. Graves Die C; ASTM D642-54 |
| Abrasion | 52 | 52 | NBS Abrasion Index; ASTM D1630-74. |
| Compression Set | 69 % @Temperature 70.0 °C | 69 % @Temperature 158 °F | 22 hr at 70°C. Method B. ASTM D395-69 |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -5.00 °C | 23.0 °F | Brittleness Temperature |
| Brittleness Temperature | -5.00 °C | 23.0 °F | ASTM D746-79 |
| Clash Berg Stiffness Temperature | 4.00 °C | 39.2 °F | T-10000 Torsional stiffness ASTM D1043-72(1981) |