- 脆化温度 [℃]: -35.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.00 g/cc | 2.00 g/cc | |||
| Mooney Viscosity | 80 @Temperature 121 °C | 80 @Temperature 250 °F | ML 1+10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 71 | 71 | Press cure 15 Minutes @ 188°C, Post Cure 24 Hours @ 250°C; ASTM D2240 | ||
| Tensile Strength at Break | 11.9 MPa | 1730 psi | Press cure 15 Minutes @ 188°C, Post Cure 24 Hours @ 250°C | ||
| Elongation at Break | 230 % | 230 % | Press cure 15 Minutes @ 188°C, Post Cure 24 Hours @ 250°C | ||
| 100% Modulus | 0.00470 GPa | 0.682 ksi | Press cure 15 Minutes @ 188°C, Post Cure 24 Hours @ 250°C | ||
| Compression Set | 27 % @Treatment Temp. 232 °C, Time 252000 sec | 27 % @Treatment Temp. 450 °F, Time 70.0 hour | Method B, -214 O-rings, Aged 70 Hours, 25% Deformation; ASTM D395 | ||
| 35 % @Treatment Temp. 232 °C, Time 605000 sec | 35 % @Treatment Temp. 450 °F, Time 168 hour | Method B, -214 O-rings, Aged 168 Hours, 25% Deformation; ASTM D395 | |||
| 50 % @Treatment Temp. 300 °C, Time 252000 sec | 50 % @Treatment Temp. 572 °F, Time 70.0 hour | Method B, -214 O-rings, Aged 70 Hours, 18% Deformation; ASTM D395 | |||
| 61 % @Treatment Temp. 300 °C, Time 605000 sec | 61 % @Treatment Temp. 572 °F, Time 168 hour | Method B, -214 O-rings, Aged 168 Hours, 18% Deformation; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 315 °C | 599 °F | |||
| Brittleness Temperature | -35.0 °C | -31.0 °F | |||
| Transformation Temperature | -2.00 °C | 28.4 °F | TR10 | ||
| Descriptive Properties | |||||
| Color | White | ||||
| Form | Crumb | ||||
| MH, Maximum Toque | 10.1 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||
| ML, Minimum Torque | 0.9 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||
| t2, Time to 2 Inch-lb Rise from Minimum | 3.4 Minute | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||
| t'50, Time to 50% Cure | 4.7 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||
| t'90, Time to 90% Cure | 8.4 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||