| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Mooney Viscosity | 36.5 @Temperature 121 °C | 36.5 @Temperature 250 °F | MS 1+60, Minimum Viscosity | ||
| >= 60 @Temperature 121 °C | >= 60 @Temperature 250 °F | MS 1+60, ts3 | |||
| >= 60 @Temperature 121 °C | >= 60 @Temperature 250 °F | MS 1+60, t310 | |||
| >= 60 @Temperature 121 °C | >= 60 @Temperature 250 °F | MS 1+60, t318 | |||
| 77.2 @Temperature 121 °C | 77.2 @Temperature 250 °F | MS 1+60, Initial Viscosity | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 71 | 71 | Press Cure 10 Minutes @ 350°C | ||
| 73 | 73 | Heat Age Resistance, 70 Hour @ 270°C | |||
| 74 | 74 | Post Cure 16 Hours @ 232°C | |||
| Tensile Strength at Break | 9.45 MPa | 1370 psi | Press Cure 10 Minutes @ 350°C | ||
| 12.14 MPa | 1761 psi | Heat Age Resistance, 70 Hour @ 270°C | |||
| 14.41 MPa | 2090 psi | Post Cure 16 Hours @ 232°C | |||
| Elongation at Break | 193 % | 193 % | Heat Age Resistance, 70 Hour @ 270°C | ||
| 206 % | 206 % | Post Cure 16 Hours @ 232°C | |||
| 266 % | 266 % | Press Cure 10 Minutes @ 350°C | |||
| 100% Modulus | 0.00439 GPa | 0.637 ksi | Press Cure 10 Minutes @ 350°C | ||
| 0.00543 GPa | 0.788 ksi | Heat Age Resistance, 70 Hour @ 270°C | |||
| 0.00621 GPa | 0.901 ksi | Post Cure 16 Hours @ 232°C | |||
| Compression Set | 13.6 % @Treatment Temp. 200 °C, Time 252000 sec | 13.6 % @Treatment Temp. 392 °F, Time 70.0 hour | -214 O-rings, Aged 70 Hours, 25% Deformation | ||
| Descriptive Properties | |||||
| MH, Maximum Toque | 22.91 inch-lb | 177°C for 12 Minutes | |||
| ML, Minimum Torque | 1.35 inch-lb | 177°C for 12 Minutes | |||
| t2, Time to 2 Inch-lb Rise from Minimum | 2.48 Minute | 177°C for 12 Minutes | |||
| t'50, Time to 50% Cure | 3.04 Minutes | 177°C for 12 Minutes | |||
| t'90, Time to 90% Cure | 4.24 Minutes | 177°C for 12 Minutes | |||