- 透光率 [%]: 25.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.88 g/cc | 1.88 g/cc | |||
| Mooney Viscosity | 37 @Temperature 121 °C | 37 @Temperature 250 °F | ML 1+10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 75 | 75 | Press cure 10 minutes@ 177°C | ||
| 78 | 78 | Post cure 2 hours @ 232°C | |||
| Tensile Strength at Break | 16.4 MPa | 2380 psi | Press cure 10 minutes@ 177°C | ||
| 22.7 MPa | 3290 psi | Post cure 2 hours @ 232°C | |||
| Elongation at Break | 220 % | 220 % | Post cure 2 hours @ 232°C | ||
| 230 % | 230 % | Press cure 10 minutes@ 177°C | |||
| 100% Modulus | 0.00480 GPa | 0.696 ksi | Press cure 10 minutes@ 177°C | ||
| 0.00630 GPa | 0.914 ksi | Post cure 2 hours @ 232°C | |||
| Compression Set | 40 % @Treatment Temp. 200 °C, Time 252000 sec | 40 % @Treatment Temp. 392 °F, Time 70.0 hour | ASTM D395 Method B | ||
| Thermal Properties | Metric | English | Comments | ||
| Transformation Temperature | -7.00 °C | 19.4 °F | ASTM D1329 | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 25 % | 25 % | translucent, but thickness not quantified | ||
| Component Elements Properties | Metric | English | Comments | ||
| Fluorine, F | 69.5 % | 69.5 % | |||
| Descriptive Properties | |||||
| Color | Translucent | ||||
| MH, Maximum Toque | 18.8 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||
| ML, Minimum Torque | 0.9 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||
| t2, Time to 2 Inch-lb Rise from Minimum | 0.4 Minute | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||
| t'50, Time to 50% Cure | 0.6 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||
| t'90, Time to 90% Cure | 1.9 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||