- 透光率 [%]: 25.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.10 g/cc | 2.10 g/cc | |||
| Mooney Viscosity | 110 @Temperature 121 °C | 110 @Temperature 250 °F | ML 1+10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 72 | 72 | Press cure 10 Minutes @ 165°C, Ramp Post Cure in Air ASTM Die D Dumbbells | ||
| 70 @Treatment Temp. 300 °C, Time 1.21e+6 sec | 70 @Treatment Temp. 572 °F, Time 336 hour | ||||
| Tensile Strength at Break | 18.9 MPa | 2740 psi | Press cure 10 Minutes @ 165°C, Ramp Post Cure in Air ASTM Die D Dumbbells | ||
| Elongation at Break | 260 % | 260 % | Press cure 10 Minutes @ 165°C, Ramp Post Cure in Air ASTM Die D Dumbbells | ||
| 100% Modulus | 0.00360 GPa | 0.522 ksi | Press cure 10 Minutes @ 165°C, Ramp Post Cure in Air ASTM Die D Dumbbells | ||
| Compression Set | 26 % @Treatment Temp. 250 °C | 26 % @Treatment Temp. 482 °F | Method B, -214 O-rings; ASTM D395 | ||
| 21 % @Treatment Temp. 230 °C, Time 252000 sec | 21 % @Treatment Temp. 446 °F, Time 70.0 hour | Method B, -214 O-rings; ASTM D395 | |||
| 26 % @Treatment Temp. 250 °C, Time 252000 sec | 26 % @Treatment Temp. 482 °F, Time 70.0 hour | Method B, -214 O-rings; ASTM D395 | |||
| 29 % @Treatment Temp. 230 °C, Time 605000 sec | 29 % @Treatment Temp. 446 °F, Time 168 hour | Method B, -214 O-rings; ASTM D395 | |||
| 32 % @Treatment Temp. 275 °C, Time 252000 sec | 32 % @Treatment Temp. 527 °F, Time 70.0 hour | Method B, -214 O-rings; ASTM D395 | |||
| 33 % @Treatment Temp. 250 °C, Time 605000 sec | 33 % @Treatment Temp. 482 °F, Time 168 hour | Method B, -214 O-rings; ASTM D395 | |||
| 33 % @Treatment Temp. 230 °C, Time 1.21e+6 sec | 33 % @Treatment Temp. 446 °F, Time 336 hour | Method B, -214 O-rings; ASTM D395 | |||
| 38 % @Treatment Temp. 275 °C, Time 605000 sec | 38 % @Treatment Temp. 527 °F, Time 168 hour | Method B, -214 O-rings; ASTM D395 | |||
| 40 % @Treatment Temp. 250 °C, Time 1.21e+6 sec | 40 % @Treatment Temp. 482 °F, Time 336 hour | Method B, -214 O-rings; ASTM D395 | |||
| 52 % @Treatment Temp. 275 °C, Time 1.21e+6 sec | 52 % @Treatment Temp. 527 °F, Time 336 hour | Method B, -214 O-rings; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 300 °C | 572 °F | |||
| 350 °C | 662 °F | peak | |||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 25 % | 25 % | translucent, but thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |||
| Die Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |||
| Head Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |||
| Screw Cooling Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Component Elements Properties | Metric | English | Comments | ||
| Fluorine, F | 73 % | 73 % | |||
| Descriptive Properties | |||||
| Color | White | ||||
| Dry Heat Resistance of Vulcanizate - 100% Modulus | 2.24 MPa | 300°C; 336 hours | |||
| 2.28 MPa | 300°C; 168 hours | ||||
| 2.41 MPa | 300°C; 70 hours | ||||
| 2.79 MPa | 275°C; 336 hours | ||||
| 3.17 MPa | 275°C; 168 hours | ||||
| 3.31 MPa | 250°C; 336 hours | ||||
| 3.41 MPa | 275°C; 70 hours | ||||
| 3.55 MPa | 250°C; 70 hours | ||||
| 3.69 MPa | 250°C; 168 hours | ||||
| Dry Heat Resistance of Vulcanizate - Elongation | 265 percent | 250°C; 168 hours | |||
| 270 percent | 250°C; 70 hours | ||||
| 280 percent | 275°C; 70 hours | ||||
| 280 percent | 275°C; 168 hours | ||||
| 290 percent | 250°C; 336 hours | ||||
| 310 percent | 275°C; 336 hours | ||||
| 335 percent | 300°C; 70 hours | ||||
| 355 percent | 300°C; 168 hours | ||||
| 380 percent | 300°C; 336 hours | ||||
| Dry Heat Resistance of Vulcanizate - Shore A Hardness | 69 | 300°C; 168 hours | |||
| 70 | 300°C; 336 hours | ||||
| 70 | 300°C; 70 hours | ||||
| 71 | 275°C; 336 hours | ||||
| 72 | 250°C; 336 hours | ||||
| 73 | 275°C; 70 hours | ||||
| 73 | 275°C; 168 hours | ||||
| 74 | 250°C; 70 hours | ||||
| 74 | 250°C; 168 hours | ||||
| Dry Heat Resistance of Vulcanizate - Tensile Strength at Break | 17.8 MPa | 300°C; 336 hours | |||
| 18.5 MPa | 300°C; 168 hours | ||||
| 18.9 MPa | 300°C; 70 hours | ||||
| 20.8 MPa | 275°C; 336 hours | ||||
| 21 MPa | 250°C; 70 hours | ||||
| 22.1 MPa | 250°C; 168 hours | ||||
| 22.4 MPa | 275°C; 70 hours | ||||
| 23 MPa | 250°C; 336 hours | ||||
| 23.6 MPa | 275°C; 168 hours | ||||
| Form | Slab | ||||
| MH, Maximum Toque | 5.9 inch-lb | 100 cpm, 0.5° Arc, 10 Minutes @ 165°C | |||
| ML, Minimum Torque | 1.9 inch-lb | 100 cpm, 0.5° Arc, 10 Minutes @ 165°C | |||
| t2, Time to 2 Inch-lb Rise from Minimum | 2.2 Minute | 100 cpm, 0.5° Arc, 10 Minutes @ 165°C | |||
| t'50, Time to 50% Cure | 2.2 Minutes | 100 cpm, 0.5° Arc, 10 Minutes @ 165°C | |||
| t'90, Time to 90% Cure | 5.8 Minutes | 100 cpm, 0.5° Arc, 10 Minutes @ 165°C | |||