- 密度 [g/cm3]: 0.9
- 弯曲强度 [MPa]: 12.4
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | A Component; ASTM D1475 |
| 1.22 g/cc | 0.0441 lb/in³ | B Component; ASTM D1475 | |
| Viscosity | 90 cP | 90 cP | A Component; ASTM D1824 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 88 | 88 | Cured property; ASTM D2240 |
| Tensile Strength, Ultimate | 12.4 MPa | 1800 psi | Cured property; ASTM D412 |
| Elongation at Break | 275 % | 275 % | Cured property; ASTM D412 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 8.50e+15 ohm-cm | 8.50e+15 ohm-cm | Cured property; ASTM D257 |
| Dielectric Constant | 3.4 @Frequency 1000 Hz | 3.4 @Frequency 1000 Hz | Cured property; ASTM D150 |
| Dielectric Strength | >= 59.1 kV/mm @Thickness 0.0508 mm | >= 1500 kV/in @Thickness 0.00200 in | Cured; ASTM D149 |
| Dissipation Factor | 0.024 @Frequency 1000 Hz | 0.024 @Frequency 1000 Hz | Cured property; ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.5 µm/m-°C @Temperature 20.0 °C | 50.3 µin/in-°F @Temperature 68.0 °F | Cured property; alpha 1; JMTP P200 |
| 197 µm/m-°C @Temperature 20.0 °C | 109 µin/in-°F @Temperature 68.0 °F | Cured property; alpha 2; JMTP P200 | |
| Glass Transition Temp, Tg | -60.0 °C | -76.0 °F | Cured property; JMTP P200 |
| Flash Point | 10.0 °C | 50.0 °F | A Component; ASTM D92 |
| 200 °C | 392 °F | B Component; ASTM D92 | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | Cure 7 days |
| 65.0 °C | 149 °F | Cure 1 hr | |
| 85.0 °C | 185 °F | Cure 30 min. | |