- 密度 [g/cm3]: 0.64
- 断裂伸长率 [%]: 38.0
- 弯曲强度 [MPa]: 19.0
- 弯曲模量 [MPa]: 1.19
- 热变形温度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.640 g/cc | 0.0231 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.640 g/cc | 0.0231 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | Bayer Test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 70 | 70 | ASTM D2240 |
| Tensile Strength, Ultimate | 19.0 MPa | 2760 psi | ASTM D638/D412 |
| Elongation at Break | 10 % | 10 % | ASTM D638/D412 |
| Flexural Yield Strength | 38.0 MPa | 5510 psi | ASTM D790 |
| Flexural Modulus | 1.19 GPa | 173 ksi | ASTM D790 |
| Compressive Yield Strength | 19.0 MPa | 2760 psi | ASTM D395 |
| Charpy Impact, Notched | 2.30 J/cm² | 10.9 ft-lb/in² | Bayer Test |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 µm/m-°C @Temperature 20.0 °C | 50.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 6.35 mm | HB @Thickness 0.250 in | |
| HB @Thickness 6.35 mm | HB @Thickness 0.250 in | ||