- 密度 [g/cm3]: 0.9
- 弯曲强度 [MPa]: 19.3
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | A Component; ASTM D1475 |
| 0.960 g/cc | 0.0347 lb/in³ | B Component; ASTM D1475 | |
| Viscosity | 30 cP | 30 cP | A Component; ASTM D1824 |
| 30 cP | 30 cP | B Component; ASTM D1824 | |
| Outgassing - Total Mass Loss | 0.84 % | 0.84 % | Cured property; at 10E-6 torr; ASTM E595 |
| Collected Volatile Condensable Material | 0.030 % | 0.030 % | Cured property; at 10E-6 torr; ASTM E595 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 88 | 88 | Cured property; ASTM D2240 |
| Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | Cured property; ASTM D412 |
| Elongation at Break | 475 % | 475 % | Cured property; ASTM D412 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | Cured property; ASTM D257 |
| Insulation Resistance | 3.20e+12 ohm | 3.20e+12 ohm | Cured property; MIL-I-46058C |
| Dielectric Constant | 3.2 @Frequency 1000 Hz | 3.2 @Frequency 1000 Hz | Cured property; ASTM D150 |
| Dielectric Strength | >= 59.1 kV/mm @Thickness 0.0762 mm | >= 1500 kV/in @Thickness 0.00300 in | Cured; ASTM D149 |
| Dissipation Factor | 0.025 @Frequency 1000 Hz | 0.025 @Frequency 1000 Hz | Cured property; ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 180 µm/m-°C @Temperature 20.0 °C | 100 µin/in-°F @Temperature 68.0 °F | Cured property; ASTM E831-86 |
| Glass Transition Temp, Tg | -74.0 °C | -101 °F | Cured property; ASTM E831-86 |
| Flash Point | 7.00 °C | 44.6 °F | A Component; ASTM D92 |
| 7.00 °C | 44.6 °F | B Component; ASTM D92 | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 85.0 °C | 185 °F | Cure 6 hrs |
| 100 °C | 212 °F | Cure 3 hrs | |
| 120 °C | 248 °F | Cure 1.5 hrs | |