- 密度 [g/cm3]: 1.69
- 吸水率 [%]: 0.09
- 弯曲强度 [MPa]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.69 g/cc | 0.0611 lb/in³ | |
| Water Absorption | 0.090 % | 0.090 % | Saturation in water |
| Water Absorption at Saturation | 0.090 % | 0.090 % | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | |
| Elongation at Break | 1.1 % | 1.1 % | |
| Tensile Modulus | 8.00 GPa | 1160 ksi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 8.00e+14 ohm-cm | 8.00e+14 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 4.5 @Frequency 1e+6 Hz | 4.5 @Frequency 1e+6 Hz | |
| 4.7 @Frequency 100 Hz | 4.7 @Frequency 100 Hz | ||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | |
| Dissipation Factor | 0.010 @Frequency 1e+6 Hz | 0.010 @Frequency 1e+6 Hz | |
| 0.025 @Frequency 100 Hz | 0.025 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 42.0 µm/m-°C @Temperature 20.0 °C | 23.3 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 42.0 µm/m-°C @Temperature 20.0 °C | 23.3 µin/in-°F @Temperature 68.0 °F | |
| Glass Transition Temp, Tg | 140 °C | 284 °F | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |
| Oxygen Index | 51 % | 51 % | |