- 弯曲强度 [MPa]: 20.7
- 弯曲模量 [MPa]: 0.241
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D412 |
| Elongation at Break | 240 % | 240 % | ASTM D412 |
| Flexural Modulus | 0.241 GPa | 35.0 ksi | ASTM D790 |
| Tear Strength | 87.7 kN/m | 500 pli | ASTM D624 |
| Heat Distortion | 360 % | 360 % | 4" Heat sag - 250°F / 60 min (1/8" thickness); ASTM D3769 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 7.22 - 73.9 °C | 45.0 - 165 °F | |
| Injection Pressure | 9.65 - 17.2 MPa | 1400 - 2500 psi | |
| Gel Time | 0.0300 min | 0.0300 min | |