- 密度 [g/cm3]: 0.64
- 弯曲强度 [MPa]: 68.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.640 g/cc | 0.0231 lb/in³ | ASTM D3574A |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 40 | 40 | ASTM D2240 |
| Tensile Strength, Ultimate | 68.6 MPa | 9950 psi | ASTM D3574E |
| Elongation at Break | 570 % | 570 % | ASTM 3457E |
| 100% Modulus | 0.00117 GPa | 0.170 ksi | ASTM D3574E |
| 200% Modulus | 0.00190 GPa | 0.276 ksi | ASTM D3574E |
| 300% Modulus | 0.00279 GPa | 0.405 ksi | ASTM D3574E |
| Compressive Yield Strength | 0.410 MPa | 59.5 psi | at 10% deflection; ASTM D3574C |
| 0.660 MPa | 95.7 psi | at 20% deflection; ASTM D3574C | |
| 0.930 MPa | 135 psi | at 30% deflection; ASTM D3574C | |
| Resilience | 35 | 35 | Bashore Rebound; ASTM 2632D |
| Tear Strength Test | 110 | 110 | lb; Die C; ASTM 3457F |