- 密度 [g/cm3]: 0.4
- 弯曲强度 [MPa]: 7.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.400 g/cc | 0.0145 lb/in³ | ASTM D3574A |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 15 | 15 | ASTM D2240 |
| Tensile Strength, Ultimate | 7.60 MPa | 1100 psi | ASTM D3574E |
| Elongation at Break | 360 % | 360 % | ASTM 3457E |
| 100% Modulus | 0.000303 GPa | 0.0439 ksi | ASTM D3574E |
| 200% Modulus | 0.000660 GPa | 0.0957 ksi | ASTM D3574E |
| Compressive Yield Strength | 0.0600 MPa | 8.70 psi | at 10% deflection; ASTM D3574C |
| 0.0900 MPa | 13.1 psi | at 20% deflection; ASTM D3574C | |
| 0.120 MPa | 17.4 psi | at 30% deflection; ASTM D3574C | |
| Resilience | 49 | 49 | Bashore Rebound; ASTM 2632D |
| Tear Strength Test | 35 | 35 | lb; Die C; ASTM 3457F |