- 拉伸强度 [MPa]: 22.54
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 62 | 62 | |||
| 80 | 80 | heat aged 70 hours @ 100ºC | |||
| Tensile Strength, Yield | 22.54 MPa | 3269 psi | |||
| Elongation at Yield | 621 % | 621 % | |||
| 100% Modulus | 0.00230 GPa | 0.334 ksi | |||
| 200% Modulus | 0.00489 GPa | 0.709 ksi | |||
| 300% Modulus | 0.008301 GPa | 1.204 ksi | |||
| Tear Strength | 56.4 kN/m | 322 pli | Die C | ||
| Compression Set | 35.8 % @Temperature 70.0 °C, Time 79200 sec | 35.8 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 7.00 min @Temperature 155 °C | 0.117 hour @Temperature 311 °F | |||
| Descriptive Properties | |||||
| Weight Loss (%) | 5 | heat aged 70 hours @ 100ºC | |||