- 拉伸强度 [MPa]: 28.1
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 63 | 63 | after 7 days at 100ºC | ||
| 65 | 65 | ||||
| Tensile Strength, Yield | 28.10 MPa | 4075 psi | after 7 days at 100ºC | ||
| 33.27 MPa | 4825 psi | ||||
| Elongation at Break | 500 % | 500 % | after 7 days at 100ºC | ||
| 570 % | 570 % | ||||
| 300% Modulus | 0.01120 GPa | 1.625 ksi | |||
| 0.0124 GPa | 1.80 ksi | after 7 days at 100ºC | |||
| Abrasion | 250 | 250 | NBS Index | ||
| Compression Set | 32 % @Temperature 70.0 °C, Time 79200 sec | 32 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 142 °C | 1.00 hour @Temperature 287 °F | |||
| Descriptive Properties | |||||
| ?T, Platen (ºC) | 75 | ||||
| Heat Build-up, Internal Temp (ºC) | 165 | Goodrich Flexometer | |||