- 拉伸强度 [MPa]: 27.9
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 65 | 65 | |||
| 68 | 68 | after 7 days at 100ºC | |||
| Tensile Strength, Yield | 27.9 MPa | 4050 psi | after 7 days at 100ºC | ||
| 31.0 MPa | 4500 psi | ||||
| Elongation at Break | 390 % | 390 % | after 7 days at 100ºC | ||
| 480 % | 480 % | ||||
| 300% Modulus | 0.01465 GPa | 2.125 ksi | |||
| 0.01948 GPa | 2.825 ksi | after 7 days at 100ºC | |||
| Abrasion | 335 | 335 | NBS Index | ||
| Compression Set | 19 % @Temperature 70.0 °C, Time 79200 sec | 19 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 142 °C | 1.00 hour @Temperature 287 °F | |||
| Descriptive Properties | |||||
| ?T, Platen (ºC) | 60 | ||||
| Heat Build-up, Internal Temp (ºC) | 135 | Goodrich Flexometer | |||