- 拉伸强度 [MPa]: 36.9
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 63 | 63 | |||
| Tensile Strength, Yield | 36.9 MPa | 5350 psi | |||
| Elongation at Yield | 570 % | 570 % | |||
| 100% Modulus | 0.00207 GPa | 0.300 ksi | |||
| 300% Modulus | 0.0103 GPa | 1.50 ksi | |||
| Tear Strength | 43.8 kN/m | 250 pli | Graves | ||
| Abrasion | 300 | 300 | NBS Index | ||
| Compression Set | 28 % @Temperature 70.0 °C, Time 79200 sec | 28 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 142 °C | 1.00 hour @Temperature 287 °F | |||
| Descriptive Properties | |||||
| 500% Modulus (ksi) | 3.5 | ||||
| Mooney Scorch | >= 30 | at 250ºF; >30 minutes to a 10 point rise | |||