- 拉伸强度 [MPa]: 18.3
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 82 | 82 | |||
| Tensile Strength, Yield | 18.3 MPa | 2650 psi | |||
| Elongation at Yield | 345 % | 345 % | |||
| 100% Modulus | 0.00601 GPa | 0.871 ksi | |||
| 200% Modulus | 0.01277 GPa | 1.852 ksi | |||
| 300% Modulus | 0.0173 GPa | 2.51 ksi | |||
| Tear Strength | 37.0 kN/m | 211 pli | Die C | ||
| Compression Set | 61 % @Temperature 70.0 °C, Time 79200 sec | 61 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 13.0 min @Temperature 160 °C | 0.217 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm³) | 122 | ||||