- 拉伸强度 [MPa]: 19.73
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 93 | 93 | |
| Tensile Strength, Yield | 19.73 MPa | 2861 psi | |
| Elongation at Yield | 343 % | 343 % | |
| 100% Modulus | 0.007288 GPa | 1.057 ksi | |
| 200% Modulus | 0.01298 GPa | 1.882 ksi | |
| 300% Modulus | 0.01708 GPa | 2.477 ksi | |
| Tear Strength | 62.1 kN/m | 354 pli | Die C |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 160 °C | 0.167 hour @Temperature 320 °F | |