- 拉伸强度 [MPa]: 13.9
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | |
| Tensile Strength, Yield | 13.9 MPa | 2020 psi | |
| Elongation at Yield | 300 % | 300 % | |
| 100% Modulus | 0.00417 GPa | 0.605 ksi | |
| 200% Modulus | 0.01059 GPa | 1.536 ksi | |
| 300% Modulus | 0.01326 GPa | 1.923 ksi | |
| Tear Strength | 26.6 kN/m | 152 pli | Die C |
| Compression Set | 20.7 % @Temperature 70.0 °C, Time 79200 sec | 20.7 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 5.00 min @Temperature 177 °C | 0.0833 hour @Temperature 350 °F | |