- 拉伸强度 [MPa]: 11.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | |
| 79 | 79 | heat aged one week at 300ºF | |
| 80 | 80 | heat aged 70 hours at 300ºF | |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | heat aged one week at 300ºF |
| 19.0 MPa | 2760 psi | heat aged 70 hours at 300ºF | |
| 28.5 MPa | 4140 psi | ||
| Elongation at Yield | 280 % | 280 % | heat aged 70 hours at 300ºF |
| 310 % | 310 % | heat aged one week at 300ºF | |
| 340 % | 340 % | ||
| 100% Modulus | 0.00427 GPa | 0.620 ksi | heat aged one week at 300ºF |
| 0.00607 GPa | 0.880 ksi | heat aged 70 hours at 300ºF | |
| 0.00910 GPa | 1.32 ksi | ||
| 200% Modulus | 0.00820 GPa | 1.19 ksi | heat aged one week at 300ºF |
| 0.0137 GPa | 1.99 ksi | heat aged 70 hours at 300ºF | |
| 0.0196 GPa | 2.84 ksi | ||
| 300% Modulus | 0.0110 GPa | 1.59 ksi | heat aged one week at 300ºF |
| 0.0270 GPa | 3.91 ksi | ||
| Processing Properties | Metric | English | Comments |
| Cure Time | 30.0 min @Temperature 152 °C | 0.500 hour @Temperature 305 °F | |