- 拉伸强度 [MPa]: 29.19
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 64 | >= 64 | |
| Tensile Strength, Yield | 29.19 MPa | 4234 psi | |
| Elongation at Yield | 562 % | 562 % | |
| 100% Modulus | 0.00260 GPa | 0.377 ksi | |
| 200% Modulus | 0.00560 GPa | 0.812 ksi | |
| 300% Modulus | 0.009797 GPa | 1.421 ksi | |
| Tear Strength | 35.2 kN/m | 201 pli | Die C |
| Compression Set | 32 % @Temperature 70.0 °C, Time 79200 sec | 32 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 12.5 min @Temperature 155 °C | 0.208 hour @Temperature 311 °F | |