- 拉伸强度 [MPa]: 30.5
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 66 | >= 66 | |
| Tensile Strength, Yield | 30.50 MPa | 4423 psi | |
| Elongation at Yield | 561 % | 561 % | |
| 100% Modulus | 0.00260 GPa | 0.377 ksi | |
| 200% Modulus | 0.00570 GPa | 0.827 ksi | |
| 300% Modulus | 0.009901 GPa | 1.436 ksi | |
| Tear Strength | 39.3 kN/m | 224 pli | Die C |
| Compression Set | 30.4 % @Temperature 70.0 °C, Time 79200 sec | 30.4 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 7.50 min @Temperature 155 °C | 0.125 hour @Temperature 311 °F | |