- 拉伸强度 [MPa]: 25.3
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 55 | >= 55 | |||
| Tensile Strength, Yield | 25.30 MPa | 3669 psi | |||
| Elongation at Yield | 607 % | 607 % | |||
| 100% Modulus | 0.00140 GPa | 0.203 ksi | |||
| 200% Modulus | 0.00230 GPa | 0.334 ksi | |||
| 300% Modulus | 0.00430 GPa | 0.624 ksi | |||
| Tear Strength | 30.3 kN/m | 173 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm³) | 87.6 | ||||