- 拉伸强度 [MPa]: 25.1
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 78 | >= 78 | |||
| Tensile Strength, Yield | 25.1 MPa | 3640 psi | |||
| Elongation at Yield | 760 % | 760 % | |||
| 100% Modulus | 0.00200 GPa | 0.290 ksi | |||
| 200% Modulus | 0.00320 GPa | 0.464 ksi | |||
| 300% Modulus | 0.00480 GPa | 0.696 ksi | |||
| Tear Strength | 32.5 kN/m | 185 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 16.0 min @Temperature 68.3 °C | 0.267 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm³) | 65.3 | ||||