- 密度 [g/cm3]: 0.0641
- 拉伸强度 [MPa]: 13.8
- 弯曲模量 [MPa]: 0.0165
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.02 g/cc | 1.02 g/cc | Part A | ||
| 1.16 g/cc | 1.16 g/cc | Mixed | |||
| 1.23 g/cc | 1.23 g/cc | Part B | |||
| Density | 0.0641 g/cc | 0.00231 lb/in³ | Free Rise Density | ||
| Viscosity | 250 cP | 250 cP | Part B | ||
| 600 cP | 600 cP | Mixed | |||
| 1000 cP | 1000 cP | Part A | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | |||
| Tensile Modulus | 0.0124 GPa | 1.80 ksi | |||
| Flexural Strength | 14.5 MPa | 2100 psi | |||
| Flexural Modulus | 0.0165 GPa | 2.40 ksi | |||
| Compressive Strength | 13.8 MPa | 2000 psi | |||
| Compressive Modulus | 0.0107 GPa | 1.55 ksi | |||
| Poissons Ratio | 0.70 - 0.75 | 0.70 - 0.75 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.00e+10 ohm-cm | 3.00e+10 ohm-cm | |||
| Dielectric Constant | 1.6 @Frequency 100 Hz, Temperature 25.0 °C | 1.6 @Frequency 100 Hz, Temperature 77.0 °F | |||
| Dielectric Strength | 13.8 kV/mm | 350 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 93.0 °C | 199 °F | Continuous | ||
| 121 °C | 250 °F | Peak | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 5.00 - 20.0 min | 0.0833 - 0.333 hour | |||
| 1440 - 4320 min @Temperature 25.0 °C | 24.0 - 72.0 hour @Temperature 77.0 °F | ||||
| Gel Time | 1.25 min | 1.25 min | |||
| Descriptive Properties | |||||
| Color | Cream | ||||
| Cream Time (seconds) | 15 | ||||
| Humidity Resistance (%) | 4.2 | 30 days at 25°C and 95RH | |||
| Mix Ratio | 1:1 | Volume | |||
| 85:100 | Weight | ||||
| Rise Time (seconds) | 90-120 | ||||
| Water Absorption (lb/ft3) | 0.66 | 30 days at 20°C | |||