- 拉伸强度 [MPa]: 4.62
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength, Yield | 4.62 MPa @Temperature 24.0 °C | 670 psi @Temperature 75.2 °F | Flatwise TS | ||
| 1710 MPa @Temperature 71.0 °C | 248000 psi @Temperature 160 °F | ||||
| 1834 MPa @Temperature 24.0 °C | 266000 psi @Temperature 75.2 °F | ||||
| Tensile Modulus | 119 GPa @Temperature 71.0 °C | 17300 ksi @Temperature 160 °F | |||
| 126.2 GPa @Temperature 24.0 °C | 18300 ksi @Temperature 75.2 °F | ||||
| Compressive Yield Strength | 1172 MPa @Temperature 71.0 °C | 170000 psi @Temperature 160 °F | |||
| 1331 MPa @Temperature 24.0 °C | 193000 psi @Temperature 75.2 °F | ||||
| Compressive Modulus | 117 GPa @Temperature 71.0 °C | 17000 ksi @Temperature 160 °F | |||
| Shear Strength | 89.6 MPa | 13000 psi | Compression interlaminar; RT | ||
| 71.7 MPa @Temperature 71.0 °C | 10400 psi @Temperature 160 °F | Compression interlaminar | |||
| Descriptive Properties | |||||
| Cured Thickness per Ply (cm) | 0.014 | Laminate | |||
| Dry Resin Content (%) | 38-40 | Prepreg | |||
| Fiber Volume (%) | 57 | Laminate | |||
| Flow (%) | 4-16 | ||||