- 拉伸强度 [MPa]: 1518.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength, Yield | 1518 MPa @Temperature 24.0 °C | 220200 psi @Temperature 75.2 °F | |||
| 1558 MPa @Temperature 71.0 °C | 226000 psi @Temperature 160 °F | ||||
| Tensile Modulus | 117 GPa @Temperature 71.0 °C | 17000 ksi @Temperature 160 °F | |||
| 124.8 GPa @Temperature 24.0 °C | 18100 ksi @Temperature 75.2 °F | ||||
| Compressive Yield Strength | 965 MPa @Temperature 71.0 °C | 140000 psi @Temperature 160 °F | |||
| 1172 MPa @Temperature 24.0 °C | 170000 psi @Temperature 75.2 °F | ||||
| Descriptive Properties | |||||
| Cured Thickness per Ply (cm) | 0.019 | Laminate | |||
| Dry Resin Content (%) | 38-40 | Prepreg | |||
| Fiber Volume (%) | 57 | Laminate | |||
| Flow (%) | 4-16 | ||||