| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | |||
| Particle Size | <= 10 µm | <= 10 µm | |||
| Viscosity | 350000 - 550000 cP @Temperature 23.0 °C | 350000 - 550000 cP @Temperature 73.4 °F | 0.5 rpm | ||
| Chemical Properties | Metric | English | Comments | ||
| Ionic Impurities - Na (Sodium) | 107 ppm | 107 ppm | |||
| Ionic Impurities - K (Potassium) | 2.0 ppm | 2.0 ppm | |||
| Ionic Impurities - Cl (Chloride) | 50 ppm | 50 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 80 | 80 | |||
| Tensile Modulus | 7.79 GPa | 1130 ksi | Storage | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 46.0 µm/m-°C | 25.6 µin/in-°F | Below Tg | ||
| 139 µm/m-°C | 77.2 µin/in-°F | Above Tg | |||
| Thermal Conductivity | 0.760 W/m-K | 5.27 BTU-in/hr-ft²-°F | |||
| Maximum Service Temperature, Air | 300 °C | 572 °F | Continuous | ||
| 400 °C | 752 °F | Intermittent | |||
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | Continuous | ||
| -55.0 °C | -67.0 °F | Intermittent | |||
| Glass Transition Temp, Tg | >= 200 °C | >= 392 °F | Cure 150ºC/1 hour + 275ºC/1 hours; Ramp 20°C/min to 350ºC | ||
| Decomposition Temperature | 519 °C | 966 °F | Degradation Temperature | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 150 °C | 1.00 hour @Temperature 302 °F | + 275°C, Minimum, Pre-Bake | ||
| Shelf Life | 12.0 Month @Temperature 25.0 °C | 12.0 Month @Temperature 77.0 °F | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Consistency | Smooth paste | ||||
| Die Shear | 3.8 kg | ||||
| Ionic Impurities NH4 | 27 ppm | ||||
| Number of Components | Single | ||||
| Thixotropic Index | >1.3 | between 0.5 & 1 rpm | |||
| Weight Loss | 0.22% | 200°C | |||
| 0.23% | 250°C | ||||
| 0.29% | 300°C | ||||