- 密度 [g/cm3]: 0.11
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.110 g/cc | 0.00398 lb/in³ | DIN 53420, ISO 845, ASTM D 1622 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 3.70 MPa | 537 psi | DIN 53455, ISO 527-2, ASTM D 638 |
| Elongation at Break | 3.0 % | 3.0 % | DIN 53455, ISO 527-2, ASTM D 638 |
| Modulus of Elasticity | 0.180 GPa | 26.1 ksi | ISO 527-2, ASTM D 638 |
| Flexural Strength | 5.20 MPa | 754 psi | DIN 53423, ISO 1209, ASTM D 790 |
| Compressive Strength | 3.60 MPa | 522 psi | DIN 53421, ISO 844, ASTM D 1621 |
| Poissons Ratio | 0.29 | 0.29 | Calculated |
| Shear Modulus | 0.0700 GPa | 10.2 ksi | DIN 53294, ASTM C 273 |
| Shear Strength | 2.40 MPa | 348 psi | DIN 53294, ASTM C 273 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat Distortion Resistance; DIN 53424 |