- 熔体流动速率 [g/10min]: 13.0
- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 0.5
- 拉伸强度 [MPa]: 40.0
- 热变形温度 [℃]: 110.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 | ||
| 1.02 g/cc @Temperature 260 °C | 0.0368 lb/in³ @Temperature 500 °F | Melt | |||
| Water Absorption | 0.50 % | 0.50 % | Similar to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | Similar to ISO 62 | ||
| Melt Flow | 13 g/10 min @Load 5.00 kg, Temperature 260 °C | 13 g/10 min @Load 11.0 lb, Temperature 500 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 1.80 GPa | 261 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 6.90 J/cm² | 32.8 ft-lb/in² | ISO 179/1eA | ||
| Tensile Creep Modulus, 1 hour | 1500 MPa | 218000 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 1200 MPa | 174000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz | 2.9 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.1 @Frequency 100 Hz | 3.1 @Frequency 100 Hz | IEC 60250 | |||
| Dissipation Factor | 0.0023 @Frequency 100 Hz | 0.0023 @Frequency 100 Hz | IEC 60250 | ||
| 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
| Specific Heat Capacity | 1.88 J/g-°C | 0.449 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.185 W/m-K | 1.28 BTU-in/hr-ft²-°F | Melt | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 119 °C | 246 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695-11-10 | |||
| Oxygen Index | 20 % | 20 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |||
| 260 °C | 500 °F | Injection Molding; ISO 294 | |||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| 70.0 °C | 158 °F | Injection Molding; ISO 10724 | |||
| Ejection Temperature | 170 °C | 338 °F | |||
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 | ||
| Descriptive Properties | |||||
| Availability | Asia Pacific | ||||
| Europe | |||||
| India | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Eff. thermal diffusivity (m²/s) | 9.6E-08 | ||||
| Feature | Release agent | ||||
| Form | Pellets | ||||
| Process | Injection Molding | ||||