- 熔体流动速率 [g/10min]: 31.9
- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.4
- 拉伸强度 [MPa]: 118.0
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H. | ||
| Viscosity Test | 96 cm³/g | 96 cm³/g | Viscosity Number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0048 cm/cm | 0.0048 in/in | 60x60x2mm; ISO 294 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | 60x60x2mm; ISO 294 | ||
| Melt Flow | 31.9 g/10 min @Load 2.16 kg, Temperature 250 °C | 31.9 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 118 MPa | 17100 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | 3.2 % | 3.2 % | 5mm/min; ISO 527 | ||
| Modulus of Elasticity | 6.90 GPa | 1000 ksi | ISO 527-2 | ||
| Tensile Modulus | 7.11 GPa | 1030 ksi | 1mm/min; ISO 527 | ||
| Charpy Impact Unnotched | 5.10 J/cm² | 24.3 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.740 J/cm² | 3.52 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 300 V | 300 V | Test solution A; IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| Maximum Service Temperature, Air | 210 °C | 410 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection molding | ||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Descriptive Properties | |||||
| Color | Natural and Black | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||