- 熔体流动速率 [g/10min]: 11.7
- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.5
- 拉伸强度 [MPa]: 54.0
- 热变形温度 [℃]: 135.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.50 % | 0.50 % | DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | 23°C/50% R.H. | ||
| Viscosity Test | 160 cm³/g | 160 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | Sheet | ||
| 0.017 cm/cm | 0.017 in/in | 60x60x2mm; ISO 294 | |||
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | Sheet | ||
| 0.021 cm/cm | 0.021 in/in | 60x60x2mm; ISO 294 | |||
| Melt Flow | 11.7 g/10 min @Load 2.16 kg, Temperature 250 °C | 11.7 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 130 MPa | 18900 psi | ISO 2039-1 | ||
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | >= 100 % | >= 100 % | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 3.5 % | 3.5 % | 50mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 2.40 GPa | 348 ksi | ISO 527-2 | ||
| Flexural Strength | 85.0 MPa | 12300 psi | ISO 178 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA | ||
| Dart Drop, Total Energy | >= 140 J | >= 103 ft-lb | ISO 6603-1 | ||
| Tensile Creep Modulus, 1000 hours | 1100 MPa | 160000 psi | elongation <0.5%, 23°C; ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.3 @Frequency 100 Hz | 3.3 @Frequency 100 Hz | IEC 60250 | ||
| 3.3 @Frequency 1.00e+6 Hz | 3.3 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 140 kV/mm | 3560 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.0010 @Frequency 100 Hz | 0.0010 @Frequency 100 Hz | IEC 60250 | ||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 13.0 - 16.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 7.22 - 8.89 µin/in-°F @Temperature 73.4 - 176 °F | |||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | IEC 1006 | ||
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | 10 K/min | ||
| Maximum Service Temperature, Air | 120 °C | 248 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 | ||
| 140 °C | 284 °F | ||||
| 200 °C | 392 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-2 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Pipe Extrusion | ||
| 260 °C | 500 °F | for shrinkage test | |||
| 250 - 275 °C | 482 - 527 °F | Injection molding | |||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| 60.0 °C | 140 °F | for shrinkage test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| FDA | 21 CFR 177.1660 | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Extrusion | ||||
| Processing | Film Extrusion | ||||
| Injection Molding | |||||
| Other Extrusion | |||||
| Profile Extrusion | |||||
| Sheet Extrusion | |||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Light stabilized or stable to light | |||||
| U.V. stabilized or stable to weather | |||||