- 熔体流动速率 [g/10min]: 24.0
- 缺口冲击强度: 8.01
- 拉伸强度 [MPa]: 59.4
- 弯曲模量 [MPa]: 2.184
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Melt Flow | 24 g/10 min @Load 5.00 kg, Temperature 265 °C | 24 g/10 min @Load 11.0 lb, Temperature 509 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 59.4 MPa | 8620 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Yield | 3.8 % | 3.8 % | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 85.8 MPa | 12400 psi | chs 0.05 in/min; ASTM D790 |
| Flexural Modulus | 2.184 GPa | 316.8 ksi | chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 15.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 138 °C @Load 1.00 kg, Thickness 3.17 mm | 280 °F @Load 2.20 lb, Thickness 0.125 in | ASTM D1525 |