- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.03
- 缺口冲击强度: 0.5
- 断裂伸长率 [%]: 140
- 弯曲强度 [MPa]: 90.0
- 弯曲模量 [MPa]: 4.50
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 - 1.52 g/cc | 0.0517 - 0.0549 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.020 cm/cm | 0.0040 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 93 | 93 | ASTM D785 |
| Tensile Strength, Ultimate | 90.0 - 110 MPa | 13100 - 16000 psi | ASTM D638 |
| Elongation at Break | 4.0 - 5.5 % | 4.0 - 5.5 % | ASTM D638 |
| Flexural Yield Strength | 140 - 180 MPa | 20300 - 26100 psi | ASTM D790 |
| Flexural Modulus | 4.50 - 6.50 GPa | 653 - 943 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 - 0.700 J/cm @Thickness 6.35 mm | 0.937 - 1.31 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 60 Hz | 3.3 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm | 559 kV/in @Thickness 0.0787 in | ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60 Hz | 0.0010 @Frequency 60 Hz | ASTM D150 |
| Arc Resistance | 90 sec | 90 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 55.0 µm/m-°C @Temperature 20.0 °C | 30.6 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 225 °C | 437 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.17 mm | V-0 @Thickness 0.125 in | |