DuPont Performance Polymers Crastin® LW9330 BK851 PBT

DuPont Performance Polymers Crastin® LW9330 BK851 PBT 物性表: DuPont Performance Polymers Crastin® LW9330 BK851 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® LW9330 BK851 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® LW9330 BK851 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.42
  • 缺口冲击强度: 7.0
 
Physical PropertiesMetricEnglishComments
Density 1.42 g/cc0.0513 lb/in³ISO 1183
Filler Content 30 %30 %
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 133 MPa
@Temperature 23.0 °C		19300 psi
@Temperature 73.4 °F		ISO 527
Tensile Stress  5.18 MPa
@Strain 0.100 %,
Temperature 100 °C		751 psi
@Strain 0.100 %,
Temperature 212 °F		ISO 11403-1/-2
 7.49 MPa
@Strain 0.100 %,
Temperature 80.0 °C		1090 psi
@Strain 0.100 %,
Temperature 176 °F		ISO 11403-1/-2
 8.17 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1180 psi
@Strain 0.100 %,
Temperature 73.4 °F		ISO 11403-1/-2
 9.44 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1370 psi
@Strain 0.100 %,
Temperature -40.0 °F		ISO 11403-1/-2
 9.51 MPa
@Strain 0.200 %,
Temperature 100 °C		1380 psi
@Strain 0.200 %,
Temperature 212 °F		ISO 11403-1/-2
 13.08 MPa
@Strain 0.300 %,
Temperature 100 °C		1897 psi
@Strain 0.300 %,
Temperature 212 °F		ISO 11403-1/-2
 14.75 MPa
@Strain 0.200 %,
Temperature 80.0 °C		2139 psi
@Strain 0.200 %,
Temperature 176 °F		ISO 11403-1/-2
 17.33 MPa
@Strain 0.200 %,
Temperature 23.0 °C		2514 psi
@Strain 0.200 %,
Temperature 73.4 °F		ISO 11403-1/-2
 18.94 MPa
@Strain 0.200 %,
Temperature -40.0 °C		2747 psi
@Strain 0.200 %,
Temperature -40.0 °F		ISO 11403-1/-2
 20.38 MPa
@Strain 0.500 %,
Temperature 100 °C		2956 psi
@Strain 0.500 %,
Temperature 212 °F		ISO 11403-1/-2
 20.83 MPa
@Strain 0.300 %,
Temperature 80.0 °C		3021 psi
@Strain 0.300 %,
Temperature 176 °F		ISO 11403-1/-2
 23.72 MPa
@Strain 0.600 %,
Temperature 100 °C		3440 psi
@Strain 0.600 %,
Temperature 212 °F		ISO 11403-1/-2
 26.42 MPa
@Strain 0.300 %,
Temperature 23.0 °C		3832 psi
@Strain 0.300 %,
Temperature 73.4 °F		ISO 11403-1/-2
 26.52 MPa
@Strain 0.700 %,
Temperature 100 °C		3846 psi
@Strain 0.700 %,
Temperature 212 °F		ISO 11403-1/-2
 28.75 MPa
@Strain 0.800 %,
Temperature 100 °C		4170 psi
@Strain 0.800 %,
Temperature 212 °F		ISO 11403-1/-2
 28.9 MPa
@Strain 0.300 %,
Temperature -40.0 °C		4190 psi
@Strain 0.300 %,
Temperature -40.0 °F		ISO 11403-1/-2
 30.54 MPa
@Strain 0.900 %,
Temperature 100 °C		4429 psi
@Strain 0.900 %,
Temperature 212 °F		ISO 11403-1/-2
 32.05 MPa
@Strain 0.500 %,
Temperature 80.0 °C		4648 psi
@Strain 0.500 %,
Temperature 176 °F		ISO 11403-1/-2
 32.16 MPa
@Strain 1.00 %,
Temperature 100 °C		4664 psi
@Strain 1.00 %,
Temperature 212 °F		ISO 11403-1/-2
 33.48 MPa
@Strain 1.10 %,
Temperature 100 °C		4856 psi
@Strain 1.10 %,
Temperature 212 °F		ISO 11403-1/-2
 34.63 MPa
@Strain 1.20 %,
Temperature 100 °C		5023 psi
@Strain 1.20 %,
Temperature 212 °F		ISO 11403-1/-2
 35.64 MPa
@Strain 1.30 %,
Temperature 100 °C		5169 psi
@Strain 1.30 %,
Temperature 212 °F		ISO 11403-1/-2
 36.35 MPa
@Strain 0.600 %,
Temperature 80.0 °C		5272 psi
@Strain 0.600 %,
Temperature 176 °F		ISO 11403-1/-2
 36.46 MPa
@Strain 1.40 %,
Temperature 100 °C		5288 psi
@Strain 1.40 %,
Temperature 212 °F		ISO 11403-1/-2
 37.08 MPa
@Strain 1.50 %,
Temperature 100 °C		5378 psi
@Strain 1.50 %,
Temperature 212 °F		ISO 11403-1/-2
 37.65 MPa
@Strain 1.60 %,
Temperature 100 °C		5461 psi
@Strain 1.60 %,
Temperature 212 °F		ISO 11403-1/-2
 38.11 MPa
@Strain 1.70 %,
Temperature 100 °C		5527 psi
@Strain 1.70 %,
Temperature 212 °F		ISO 11403-1/-2
 38.57 MPa
@Strain 1.80 %,
Temperature 100 °C		5594 psi
@Strain 1.80 %,
Temperature 212 °F		ISO 11403-1/-2
 39.06 MPa
@Strain 1.90 %,
Temperature 100 °C		5665 psi
@Strain 1.90 %,
Temperature 212 °F		ISO 11403-1/-2
 39.51 MPa
@Strain 2.00 %,
Temperature 100 °C		5730 psi
@Strain 2.00 %,
Temperature 212 °F		ISO 11403-1/-2
 39.99 MPa
@Strain 2.10 %,
Temperature 100 °C		5800 psi
@Strain 2.10 %,
Temperature 212 °F		ISO 11403-1/-2
 40.07 MPa
@Strain 0.700 %,
Temperature 80.0 °C		5812 psi
@Strain 0.700 %,
Temperature 176 °F		ISO 11403-1/-2
 40.44 MPa
@Strain 2.20 %,
Temperature 100 °C		5865 psi
@Strain 2.20 %,
Temperature 212 °F		ISO 11403-1/-2
 40.83 MPa
@Strain 2.30 %,
Temperature 100 °C		5922 psi
@Strain 2.30 %,
Temperature 212 °F		ISO 11403-1/-2
 41.13 MPa
@Strain 2.40 %,
Temperature 100 °C		5965 psi
@Strain 2.40 %,
Temperature 212 °F		ISO 11403-1/-2
 41.41 MPa
@Strain 2.50 %,
Temperature 100 °C		6006 psi
@Strain 2.50 %,
Temperature 212 °F		ISO 11403-1/-2
 41.65 MPa
@Strain 2.60 %,
Temperature 100 °C		6041 psi
@Strain 2.60 %,
Temperature 212 °F		ISO 11403-1/-2
 41.86 MPa
@Strain 2.70 %,
Temperature 100 °C		6071 psi
@Strain 2.70 %,
Temperature 212 °F		ISO 11403-1/-2
 42.05 MPa
@Strain 2.80 %,
Temperature 100 °C		6099 psi
@Strain 2.80 %,
Temperature 212 °F		ISO 11403-1/-2
 42.21 MPa
@Strain 2.90 %,
Temperature 100 °C		6122 psi
@Strain 2.90 %,
Temperature 212 °F		ISO 11403-1/-2
 42.33 MPa
@Strain 3.90 %,
Temperature 100 °C		6139 psi
@Strain 3.90 %,
Temperature 212 °F		ISO 11403-1/-2
 42.37 MPa
@Strain 3.00 %,
Temperature 100 °C		6145 psi
@Strain 3.00 %,
Temperature 212 °F		ISO 11403-1/-2
 42.48 MPa
@Strain 3.10 %,
Temperature 100 °C		6161 psi
@Strain 3.10 %,
Temperature 212 °F		ISO 11403-1/-2
 42.59 MPa
@Strain 3.20 %,
Temperature 100 °C		6177 psi
@Strain 3.20 %,
Temperature 212 °F		ISO 11403-1/-2
 42.63 MPa
@Strain 3.80 %,
Temperature 100 °C		6183 psi
@Strain 3.80 %,
Temperature 212 °F		ISO 11403-1/-2
 42.66 MPa
@Strain 3.30 %,
Temperature 100 °C		6187 psi
@Strain 3.30 %,
Temperature 212 °F		ISO 11403-1/-2
 42.71 MPa
@Strain 3.40 %,
Temperature 100 °C		6195 psi
@Strain 3.40 %,
Temperature 212 °F		ISO 11403-1/-2
 42.71 MPa
@Strain 3.70 %,
Temperature 100 °C		6195 psi
@Strain 3.70 %,
Temperature 212 °F		ISO 11403-1/-2
 42.75 MPa
@Strain 3.50 %,
Temperature 100 °C		6200 psi
@Strain 3.50 %,
Temperature 212 °F		ISO 11403-1/-2
 42.75 MPa
@Strain 3.60 %,
Temperature 100 °C		6200 psi
@Strain 3.60 %,
Temperature 212 °F		ISO 11403-1/-2
 43.98 MPa
@Strain 0.800 %,
Temperature 80.0 °C		6379 psi
@Strain 0.800 %,
Temperature 176 °F		ISO 11403-1/-2
 44.12 MPa
@Strain 0.500 %,
Temperature 23.0 °C		6399 psi
@Strain 0.500 %,
Temperature 73.4 °F		ISO 11403-1/-2
 47.48 MPa
@Strain 0.900 %,
Temperature 80.0 °C		6886 psi
@Strain 0.900 %,
Temperature 176 °F		ISO 11403-1/-2
 50.0 MPa
@Strain 0.500 %,
Temperature -40.0 °C		7250 psi
@Strain 0.500 %,
Temperature -40.0 °F		ISO 11403-1/-2
 50.45 MPa
@Strain 1.00 %,
Temperature 80.0 °C		7317 psi
@Strain 1.00 %,
Temperature 176 °F		ISO 11403-1/-2
 53.04 MPa
@Strain 1.10 %,
Temperature 80.0 °C		7693 psi
@Strain 1.10 %,
Temperature 176 °F		ISO 11403-1/-2
 54.45 MPa
@Strain 0.600 %,
Temperature 23.0 °C		7897 psi
@Strain 0.600 %,
Temperature 73.4 °F		ISO 11403-1/-2
 55.36 MPa
@Strain 1.20 %,
Temperature 80.0 °C		8029 psi
@Strain 1.20 %,
Temperature 176 °F		ISO 11403-1/-2
 57.42 MPa
@Strain 1.30 %,
Temperature 80.0 °C		8328 psi
@Strain 1.30 %,
Temperature 176 °F		ISO 11403-1/-2
 59.16 MPa
@Strain 1.40 %,
Temperature 80.0 °C		8580 psi
@Strain 1.40 %,
Temperature 176 °F		ISO 11403-1/-2
 59.58 MPa
@Strain 0.600 %,
Temperature -40.0 °C		8641 psi
@Strain 0.600 %,
Temperature -40.0 °F		ISO 11403-1/-2
 60.64 MPa
@Strain 1.50 %,
Temperature 80.0 °C		8795 psi
@Strain 1.50 %,
Temperature 176 °F		ISO 11403-1/-2
 61.93 MPa
@Strain 1.60 %,
Temperature 80.0 °C		8982 psi
@Strain 1.60 %,
Temperature 176 °F		ISO 11403-1/-2
 62.99 MPa
@Strain 1.70 %,
Temperature 80.0 °C		9136 psi
@Strain 1.70 %,
Temperature 176 °F		ISO 11403-1/-2
 63.89 MPa
@Strain 1.80 %,
Temperature 80.0 °C		9266 psi
@Strain 1.80 %,
Temperature 176 °F		ISO 11403-1/-2
 63.89 MPa
@Strain 0.700 %,
Temperature 23.0 °C		9266 psi
@Strain 0.700 %,
Temperature 73.4 °F		ISO 11403-1/-2
 64.46 MPa
@Strain 1.90 %,
Temperature 80.0 °C		9349 psi
@Strain 1.90 %,
Temperature 176 °F		ISO 11403-1/-2
 69.39 MPa
@Strain 0.700 %,
Temperature -40.0 °C		10060 psi
@Strain 0.700 %,
Temperature -40.0 °F		ISO 11403-1/-2
 72.69 MPa
@Strain 0.800 %,
Temperature 23.0 °C		10540 psi
@Strain 0.800 %,
Temperature 73.4 °F		ISO 11403-1/-2
 79.1 MPa
@Strain 0.800 %,
Temperature -40.0 °C		11500 psi
@Strain 0.800 %,
Temperature -40.0 °F		ISO 11403-1/-2
 80.89 MPa
@Strain 0.900 %,
Temperature 23.0 °C		11730 psi
@Strain 0.900 %,
Temperature 73.4 °F		ISO 11403-1/-2
 88.52 MPa
@Strain 1.00 %,
Temperature 23.0 °C		12840 psi
@Strain 1.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 88.57 MPa
@Strain 0.900 %,
Temperature -40.0 °C		12850 psi
@Strain 0.900 %,
Temperature -40.0 °F		ISO 11403-1/-2
 95.51 MPa
@Strain 1.10 %,
Temperature 23.0 °C		13850 psi
@Strain 1.10 %,
Temperature 73.4 °F		ISO 11403-1/-2
 97.79 MPa
@Strain 1.00 %,
Temperature -40.0 °C		14180 psi
@Strain 1.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 102.04 MPa
@Strain 1.20 %,
Temperature 23.0 °C		14800 psi
@Strain 1.20 %,
Temperature 73.4 °F		ISO 11403-1/-2
 106.55 MPa
@Strain 1.10 %,
Temperature -40.0 °C		15454 psi
@Strain 1.10 %,
Temperature -40.0 °F		ISO 11403-1/-2
 108.13 MPa
@Strain 1.30 %,
Temperature 23.0 °C		15683 psi
@Strain 1.30 %,
Temperature 73.4 °F		ISO 11403-1/-2
 115 MPa
@Strain 1.20 %,
Temperature -40.0 °C		16700 psi
@Strain 1.20 %,
Temperature -40.0 °F		ISO 11403-1/-2
 123.16 MPa
@Strain 1.30 %,
Temperature -40.0 °C		17863 psi
@Strain 1.30 %,
Temperature -40.0 °F		ISO 11403-1/-2
 131.31 MPa
@Strain 1.40 %,
Temperature -40.0 °C		19045 psi
@Strain 1.40 %,
Temperature -40.0 °F		ISO 11403-1/-2
 138.91 MPa
@Strain 1.50 %,
Temperature -40.0 °C		20147 psi
@Strain 1.50 %,
Temperature -40.0 °F		ISO 11403-1/-2
 145.85 MPa
@Strain 1.60 %,
Temperature -40.0 °C		21154 psi
@Strain 1.60 %,
Temperature -40.0 °F		ISO 11403-1/-2
 152.76 MPa
@Strain 1.70 %,
Temperature -40.0 °C		22156 psi
@Strain 1.70 %,
Temperature -40.0 °F		ISO 11403-1/-2
 159.43 MPa
@Strain 1.80 %,
Temperature -40.0 °C		23123 psi
@Strain 1.80 %,
Temperature -40.0 °F		ISO 11403-1/-2
 163.08 MPa
@Strain 1.90 %,
Temperature -40.0 °C		23653 psi
@Strain 1.90 %,
Temperature -40.0 °F		ISO 11403-1/-2
Elongation at Break 2.2 %
@Temperature 23.0 °C		2.2 %
@Temperature 73.4 °F		ISO 527
Tensile Modulus 9.60 GPa
@Temperature 23.0 °C		1390 ksi
@Temperature 73.4 °F		ISO 527
Izod Impact, Notched (ISO) 7.00 kJ/m²
@Temperature 23.0 °C		3.33 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Charpy Impact Unnotched 5.00 J/cm²
@Temperature 23.0 °C		23.8 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²
@Temperature 23.0 °C		3.81 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
UL RTI, Electrical  130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
UL RTI, Mechanical with Impact  125 °C
@Thickness 1.50 mm		257 °F
@Thickness 0.0591 in		UL 746B
 125 °C
@Thickness 0.750 mm		257 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
Flammability, UL94  HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
Glow Wire Test  700 °C
@Thickness 0.750 mm		1290 °F
@Thickness 0.0295 in		IEC 60695-2-12
 700 °C
@Thickness 1.50 mm		1290 °F
@Thickness 0.0591 in		IEC 60695-2-12
 725 °C
@Thickness 1.50 mm		1340 °F
@Thickness 0.0591 in		Ignition; IEC 60695-2-13
 725 °C
@Thickness 0.750 mm		1340 °F
@Thickness 0.0295 in		Ignition; IEC 60695-2-13
 775 °C
@Thickness 3.00 mm		1430 °F
@Thickness 0.118 in		IEC 60695-2-12
 800 °C
@Thickness 3.00 mm		1470 °F
@Thickness 0.118 in		Ignition; IEC 60695-2-13
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AdditiveLubricant
AppearanceBlack Color
Drying RecommendedYes
FeaturesAppearance, Pleasing Surface
 Chemical Resistance, Good
 Dimensional Stability, Good
 Moisture Absorption, Low
 Processability, Good
 Warp Resistant
 Warpage, Low
FillerGlass fiber reinforcement
FormsPellets
GenericPBT Alloy
Material StatusCurrent
Part Marking Code>PBT+SAN-GF30<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
 Low Warp Resins
Region Available - GlobalYes
Resin IdentificationPBT+SAN-GF30ISO 1043
RoHS ComplianceContact Manufacturer
UsesAutomotive Applications
 Housings
 Industrial Applications

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38073.html

免责声明: 本文 DuPont Performance Polymers Crastin® LW9330 BK851 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4