  4. DuPont Performance Polymers Crastin® SK605 NC010 PBT

DuPont Performance Polymers Crastin® SK605 NC010 PBT

DuPont Performance Polymers Crastin® SK605 NC010 PBT 物性表: DuPont Performance Polymers Crastin® SK605 NC010 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® SK605 NC010 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® SK605 NC010 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.53
  • 吸水率 [%]: 0.13
  • 缺口冲击强度: 1.01
  • 弯曲模量 [MPa]: 2.758
  • 热变形温度 [℃]: 220.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.53 g/cc1.53 g/ccASTM D792
Density 1.53 g/cc0.0553 lb/in³ISO 1183
Filler Content 30 %30 %
Water Absorption  0.13 %
@Temperature 23.0 °C		0.13 %
@Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 0.37 %
@Temperature 23.0 °C		0.37 %
@Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Viscosity  72000 cP
@Shear Rate 10000 1/s,
Temperature 260 °C		72000 cP
@Shear Rate 10000 1/s,
Temperature 500 °F		ISO 11443
 86000 cP
@Shear Rate 10000 1/s,
Temperature 250 °C		86000 cP
@Shear Rate 10000 1/s,
Temperature 482 °F		ISO 11443
 101000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		101000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		ISO 11443
 103000 cP
@Shear Rate 10000 1/s,
Temperature 240 °C		103000 cP
@Shear Rate 10000 1/s,
Temperature 464 °F		ISO 11443
 120000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		120000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		ISO 11443
 144000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		144000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		ISO 11443
 155000 cP
@Shear Rate 2000 1/s,
Temperature 260 °C		155000 cP
@Shear Rate 2000 1/s,
Temperature 500 °F		ISO 11443
 185000 cP
@Shear Rate 2000 1/s,
Temperature 250 °C		185000 cP
@Shear Rate 2000 1/s,
Temperature 482 °F		ISO 11443
 211000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C		211000 cP
@Shear Rate 1000 1/s,
Temperature 500 °F		ISO 11443
 223000 cP
@Shear Rate 2000 1/s,
Temperature 240 °C		223000 cP
@Shear Rate 2000 1/s,
Temperature 464 °F		ISO 11443
 254000 cP
@Shear Rate 1000 1/s,
Temperature 250 °C		254000 cP
@Shear Rate 1000 1/s,
Temperature 482 °F		ISO 11443
 281000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		281000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		ISO 11443
 308000 cP
@Shear Rate 1000 1/s,
Temperature 240 °C		308000 cP
@Shear Rate 1000 1/s,
Temperature 464 °F		ISO 11443
 342000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		342000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		ISO 11443
 420000 cP
@Shear Rate 500 1/s,
Temperature 240 °C		420000 cP
@Shear Rate 500 1/s,
Temperature 464 °F		ISO 11443
 463000 cP
@Shear Rate 100 1/s,
Temperature 260 °C		463000 cP
@Shear Rate 100 1/s,
Temperature 500 °F		ISO 11443
 594000 cP
@Shear Rate 100 1/s,
Temperature 250 °C		594000 cP
@Shear Rate 100 1/s,
Temperature 482 °F		ISO 11443
 768000 cP
@Shear Rate 100 1/s,
Temperature 240 °C		768000 cP
@Shear Rate 100 1/s,
Temperature 464 °F		ISO 11443
Linear Mold Shrinkage 0.0030 cm/cm0.0030 in/inFlow
 0.010 cm/cm0.010 in/inTransverse
Linear Mold Shrinkage, Flow 0.0040 cm/cm0.0040 in/inParallel; Annealed; ISO 294-4
 0.0030 cm/cm
@Thickness 2.00 mm		0.0030 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0135 cm/cm0.0135 in/inNormal; Annealed; ISO 294-4
 0.011 cm/cm
@Thickness 2.00 mm		0.011 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
Melt Index of Compound 5.0 g/10 min
@Load 2.16 kg,
Temperature 250 °C		5.0 g/10 min
@Load 4.76 lb,
Temperature 482 °F		cm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  57.0 MPa
@Temperature 150 °C		8270 psi
@Temperature 302 °F		ISO 527
 70.0 MPa
@Temperature 120 °C		10200 psi
@Temperature 248 °F		ISO 527
 140 MPa
@Temperature 23.0 °C		20300 psi
@Temperature 73.4 °F		ISO 527
 222 MPa
@Temperature -40.0 °C		32200 psi
@Temperature -40.0 °F		ISO 527
Tensile Strength  54.0 MPa
@Temperature 149 °C		7830 psi
@Temperature 300 °F		ASTM D638
 76.0 MPa
@Temperature 90.0 °C		11000 psi
@Temperature 194 °F		ASTM D638
 140 MPa
@Temperature 23.0 °C		20300 psi
@Temperature 73.4 °F		ASTM D638
 207 MPa
@Temperature -40.0 °C		30000 psi
@Temperature -40.0 °F		ASTM D638
Tensile Stress  8.08 MPa
@Strain 0.250 %,
Temperature 160 °C		1170 psi
@Strain 0.250 %,
Temperature 320 °F		ISO 527
 10.3 MPa
@Strain 0.250 %,
Temperature 120 °C		1490 psi
@Strain 0.250 %,
Temperature 248 °F		ISO 527
 11.1 MPa
@Strain 0.250 %,
Temperature 100 °C		1610 psi
@Strain 0.250 %,
Temperature 212 °F		ISO 527
 12.1 MPa
@Strain 0.250 %,
Temperature 80.0 °C		1750 psi
@Strain 0.250 %,
Temperature 176 °F		ISO 527
 14.5 MPa
@Strain 0.250 %,
Temperature 60.0 °C		2100 psi
@Strain 0.250 %,
Temperature 140 °F		ISO 527
 14.6 MPa
@Strain 0.500 %,
Temperature 160 °C		2120 psi
@Strain 0.500 %,
Temperature 320 °F		ISO 527
 18.7 MPa
@Strain 0.500 %,
Temperature 120 °C		2710 psi
@Strain 0.500 %,
Temperature 248 °F		ISO 527
 20.3 MPa
@Strain 0.500 %,
Temperature 100 °C		2940 psi
@Strain 0.500 %,
Temperature 212 °F		ISO 527
 22.3 MPa
@Strain 0.500 %,
Temperature 80.0 °C		3230 psi
@Strain 0.500 %,
Temperature 176 °F		ISO 527
 22.5 MPa
@Strain 0.250 %,
Temperature 40.0 °C		3260 psi
@Strain 0.250 %,
Temperature 104 °F		ISO 527
 24.1 MPa
@Strain 1.00 %,
Temperature 160 °C		3500 psi
@Strain 1.00 %,
Temperature 320 °F		ISO 527
 24.9 MPa
@Strain 0.250 %,
Temperature 23.0 °C		3610 psi
@Strain 0.250 %,
Temperature 73.4 °F		ISO 527
 27.6 MPa
@Strain 0.500 %,
Temperature 60.0 °C		4000 psi
@Strain 0.500 %,
Temperature 140 °F		ISO 527
 28.9 MPa
@Strain 0.250 %,
Temperature 0.000 °C		4190 psi
@Strain 0.250 %,
Temperature 32.0 °F		ISO 527
 30.0 MPa
@Strain 0.250 %,
Temperature -20.0 °C		4350 psi
@Strain 0.250 %,
Temperature -4.00 °F		ISO 527
 30.7 MPa
@Strain 1.50 %,
Temperature 160 °C		4450 psi
@Strain 1.50 %,
Temperature 320 °F		ISO 527
 30.7 MPa
@Strain 0.250 %,
Temperature -40.0 °C		4450 psi
@Strain 0.250 %,
Temperature -40.0 °F		ISO 527
 31.5 MPa
@Strain 1.00 %,
Temperature 120 °C		4570 psi
@Strain 1.00 %,
Temperature 248 °F		ISO 527
 34.3 MPa
@Strain 1.00 %,
Temperature 100 °C		4970 psi
@Strain 1.00 %,
Temperature 212 °F		ISO 527
 35.4 MPa
@Strain 2.00 %,
Temperature 160 °C		5130 psi
@Strain 2.00 %,
Temperature 320 °F		ISO 527
 38.2 MPa
@Strain 1.00 %,
Temperature 80.0 °C		5540 psi
@Strain 1.00 %,
Temperature 176 °F		ISO 527
 38.8 MPa
@Strain 2.50 %,
Temperature 160 °C		5630 psi
@Strain 2.50 %,
Temperature 320 °F		ISO 527
 40.5 MPa
@Strain 1.50 %,
Temperature 120 °C		5870 psi
@Strain 1.50 %,
Temperature 248 °F		ISO 527
 41.3 MPa
@Strain 3.00 %,
Temperature 160 °C		5990 psi
@Strain 3.00 %,
Temperature 320 °F		ISO 527
 43.1 MPa
@Strain 3.50 %,
Temperature 160 °C		6250 psi
@Strain 3.50 %,
Temperature 320 °F		Break; ISO 527
 43.9 MPa
@Strain 0.500 %,
Temperature 40.0 °C		6370 psi
@Strain 0.500 %,
Temperature 104 °F		ISO 527
 44.3 MPa
@Strain 1.50 %,
Temperature 100 °C		6430 psi
@Strain 1.50 %,
Temperature 212 °F		ISO 527
 45.9 MPa
@Strain 1.00 %,
Temperature 60.0 °C		6660 psi
@Strain 1.00 %,
Temperature 140 °F		ISO 527
 46.9 MPa
@Strain 2.00 %,
Temperature 120 °C		6800 psi
@Strain 2.00 %,
Temperature 248 °F		ISO 527
 49.5 MPa
@Strain 1.50 %,
Temperature 80.0 °C		7180 psi
@Strain 1.50 %,
Temperature 176 °F		ISO 527
 49.5 MPa
@Strain 0.500 %,
Temperature 23.0 °C		7180 psi
@Strain 0.500 %,
Temperature 73.4 °F		ISO 527
 51.5 MPa
@Strain 2.00 %,
Temperature 100 °C		7470 psi
@Strain 2.00 %,
Temperature 212 °F		ISO 527
 51.5 MPa
@Strain 2.50 %,
Temperature 120 °C		7470 psi
@Strain 2.50 %,
Temperature 248 °F		ISO 527
 54.9 MPa
@Strain 3.00 %,
Temperature 120 °C		7960 psi
@Strain 3.00 %,
Temperature 248 °F		ISO 527
 56.5 MPa
@Strain 0.500 %,
Temperature 0.000 °C		8190 psi
@Strain 0.500 %,
Temperature 32.0 °F		ISO 527
 56.8 MPa
@Strain 2.50 %,
Temperature 100 °C		8240 psi
@Strain 2.50 %,
Temperature 212 °F		ISO 527
 57.3 MPa
@Strain 3.50 %,
Temperature 120 °C		8310 psi
@Strain 3.50 %,
Temperature 248 °F		Break; ISO 527
 57.6 MPa
@Strain 2.00 %,
Temperature 80.0 °C		8350 psi
@Strain 2.00 %,
Temperature 176 °F		ISO 527
 58.9 MPa
@Strain 0.500 %,
Temperature -20.0 °C		8540 psi
@Strain 0.500 %,
Temperature -4.00 °F		ISO 527
 59.4 MPa
@Strain 1.50 %,
Temperature 60.0 °C		8620 psi
@Strain 1.50 %,
Temperature 140 °F		ISO 527
 60.5 MPa
@Strain 0.500 %,
Temperature -40.0 °C		8770 psi
@Strain 0.500 %,
Temperature -40.0 °F		ISO 527
 60.7 MPa
@Strain 3.00 %,
Temperature 100 °C		8800 psi
@Strain 3.00 %,
Temperature 212 °F		ISO 527
 63.2 MPa
@Strain 2.50 %,
Temperature 80.0 °C		9170 psi
@Strain 2.50 %,
Temperature 176 °F		ISO 527
 63.6 MPa
@Strain 3.50 %,
Temperature 100 °C		9220 psi
@Strain 3.50 %,
Temperature 212 °F		Break; ISO 527
 67.1 MPa
@Strain 3.00 %,
Temperature 80.0 °C		9730 psi
@Strain 3.00 %,
Temperature 176 °F		ISO 527
 69.1 MPa
@Strain 2.00 %,
Temperature 60.0 °C		10000 psi
@Strain 2.00 %,
Temperature 140 °F		ISO 527
 69.7 MPa
@Strain 3.50 %,
Temperature 80.0 °C		10100 psi
@Strain 3.50 %,
Temperature 176 °F		Break; ISO 527
 73.1 MPa
@Strain 1.00 %,
Temperature 40.0 °C		10600 psi
@Strain 1.00 %,
Temperature 104 °F		ISO 527
 75.9 MPa
@Strain 2.50 %,
Temperature 60.0 °C		11000 psi
@Strain 2.50 %,
Temperature 140 °F		ISO 527
 80.7 MPa
@Strain 3.00 %,
Temperature 60.0 °C		11700 psi
@Strain 3.00 %,
Temperature 140 °F		ISO 527
 83.9 MPa
@Strain 3.50 %,
Temperature 60.0 °C		12200 psi
@Strain 3.50 %,
Temperature 140 °F		Break; ISO 527
 91.7 MPa
@Strain 1.50 %,
Temperature 40.0 °C		13300 psi
@Strain 1.50 %,
Temperature 104 °F		ISO 527
 92.5 MPa
@Strain 1.00 %,
Temperature 23.0 °C		13400 psi
@Strain 1.00 %,
Temperature 73.4 °F		ISO 527
 102 MPa
@Strain 2.00 %,
Temperature 40.0 °C		14800 psi
@Strain 2.00 %,
Temperature 104 °F		ISO 527
 104 MPa
@Strain 1.00 %,
Temperature 0.000 °C		15100 psi
@Strain 1.00 %,
Temperature 32.0 °F		ISO 527
 110 MPa
@Strain 2.50 %,
Temperature 40.0 °C		16000 psi
@Strain 2.50 %,
Temperature 104 °F		ISO 527
 110 MPa
@Strain 1.00 %,
Temperature -20.0 °C		16000 psi
@Strain 1.00 %,
Temperature -4.00 °F		ISO 527
 114 MPa
@Strain 3.00 %,
Temperature 40.0 °C		16500 psi
@Strain 3.00 %,
Temperature 104 °F		ISO 527
 115 MPa
@Strain 3.50 %,
Temperature 40.0 °C		16700 psi
@Strain 3.50 %,
Temperature 104 °F		Break; ISO 527
 115 MPa
@Strain 1.00 %,
Temperature -40.0 °C		16700 psi
@Strain 1.00 %,
Temperature -40.0 °F		ISO 527
 122 MPa
@Strain 1.50 %,
Temperature 23.0 °C		17700 psi
@Strain 1.50 %,
Temperature 73.4 °F		ISO 527
 136 MPa
@Strain 2.00 %,
Temperature 23.0 °C		19700 psi
@Strain 2.00 %,
Temperature 73.4 °F		ISO 527
 138 MPa
@Strain 1.50 %,
Temperature 0.000 °C		20000 psi
@Strain 1.50 %,
Temperature 32.0 °F		ISO 527
 140 MPa
@Strain 2.60 %,
Temperature 23.0 °C		20300 psi
@Strain 2.60 %,
Temperature 73.4 °F		Break; ISO 527
 149 MPa
@Strain 1.50 %,
Temperature -20.0 °C		21600 psi
@Strain 1.50 %,
Temperature -4.00 °F		ISO 527
 159 MPa
@Strain 1.50 %,
Temperature -40.0 °C		23100 psi
@Strain 1.50 %,
Temperature -40.0 °F		ISO 527
 160 MPa
@Strain 2.00 %,
Temperature 0.000 °C		23200 psi
@Strain 2.00 %,
Temperature 32.0 °F		ISO 527
 170 MPa
@Strain 2.50 %,
Temperature 0.000 °C		24700 psi
@Strain 2.50 %,
Temperature 32.0 °F		Break; ISO 527
 176 MPa
@Strain 2.00 %,
Temperature -20.0 °C		25500 psi
@Strain 2.00 %,
Temperature -4.00 °F		ISO 527
 188 MPa
@Strain 2.30 %,
Temperature -20.0 °C		27300 psi
@Strain 2.30 %,
Temperature -4.00 °F		Break; ISO 527
 191 MPa
@Strain 2.00 %,
Temperature -40.0 °C		27700 psi
@Strain 2.00 %,
Temperature -40.0 °F		ISO 527
 200 MPa
@Strain 2.20 %,
Temperature -40.0 °C		29000 psi
@Strain 2.20 %,
Temperature -40.0 °F		Break; ISO 527
Elongation at Break  2.6 %
@Temperature 23.0 °C		2.6 %
@Temperature 73.4 °F		ASTM D638
 2.7 %
@Temperature -40.0 °C		2.7 %
@Temperature -40.0 °F		ASTM D638
 2.7 %
@Temperature 23.0 °C		2.7 %
@Temperature 73.4 °F		ISO 527
 3.2 %
@Temperature -40.0 °C		3.2 %
@Temperature -40.0 °F		ISO 527
 3.8 %
@Temperature 90.0 °C		3.8 %
@Temperature 194 °F		ASTM D638
 4.2 %
@Temperature 150 °C		4.2 %
@Temperature 302 °F		ASTM D638
 5.3 %
@Temperature 120 °C		5.3 %
@Temperature 248 °F		ISO 527
 5.7 %
@Temperature 150 °C		5.7 %
@Temperature 302 °F		ISO 527
Tensile Modulus  3.90 GPa
@Temperature 150 °C		566 ksi
@Temperature 302 °F		ISO 527
 4.65 GPa
@Temperature 120 °C		674 ksi
@Temperature 248 °F		ISO 527
 10.0 GPa
@Temperature 23.0 °C		1450 ksi
@Temperature 73.4 °F		ASTM D638
 10.0 GPa
@Temperature 23.0 °C		1450 ksi
@Temperature 73.4 °F		ISO 527
 10.9 GPa
@Temperature -40.0 °C		1580 ksi
@Temperature -40.0 °F		ISO 527
Flexural Strength  75.0 MPa
@Temperature 149 °C		10900 psi
@Temperature 300 °F		ASTM D790
 78.0 MPa
@Temperature 150 °C		11300 psi
@Temperature 302 °F		ISO 178
 93.0 MPa
@Temperature 120 °C		13500 psi
@Temperature 248 °F		ISO 178
 115 MPa
@Temperature 90.0 °C		16700 psi
@Temperature 194 °F		ASTM D790
 200 MPa
@Temperature 23.0 °C		29000 psi
@Temperature 73.4 °F		ASTM D790
 200 MPa
@Temperature 23.0 °C		29000 psi
@Temperature 73.4 °F		ISO 178
 268 MPa
@Temperature -40.0 °C		38900 psi
@Temperature -40.0 °F		ASTM D790
 286 MPa
@Temperature -40.0 °C		41500 psi
@Temperature -40.0 °F		ISO 178
Flexural Modulus  2.758 GPa
@Temperature 149 °C		400.0 ksi
@Temperature 300 °F		ASTM D790
 3.725 GPa
@Temperature 150 °C		540.3 ksi
@Temperature 302 °F		ISO 178
 3.862 GPa
@Temperature 90.0 °C		560.1 ksi
@Temperature 194 °F		ASTM D790
 4.10 GPa
@Temperature 120 °C		595 ksi
@Temperature 248 °F		ISO 178
 8.965 GPa
@Temperature 23.0 °C		1300 ksi
@Temperature 73.4 °F		ASTM D790
 9.00 GPa
@Temperature 23.0 °C		1310 ksi
@Temperature 73.4 °F		ISO 178
 9.20 GPa
@Temperature -40.0 °C		1330 ksi
@Temperature -40.0 °F		ISO 178
 9.31 GPa
@Temperature -40.0 °C		1350 ksi
@Temperature -40.0 °F		ASTM D790
Compressive Strength 202 MPa
@Thickness 3.20 mm,
Temperature 23.0 °C		29300 psi
@Thickness 0.126 in,
Temperature 73.4 °F		5mm/min (0.2in/min); ASTM D695
Shear Modulus  0.380 GPa
@Temperature 200 °C		55.1 ksi
@Temperature 392 °F		ISO 6721
 0.419 GPa
@Temperature 190 °C		60.8 ksi
@Temperature 374 °F		ISO 6721
 0.461 GPa
@Temperature 180 °C		66.9 ksi
@Temperature 356 °F		ISO 6721
 0.499 GPa
@Temperature 170 °C		72.4 ksi
@Temperature 338 °F		ISO 6721
 0.550 GPa
@Temperature 160 °C		79.8 ksi
@Temperature 320 °F		ISO 6721
 0.590 GPa
@Temperature 150 °C		85.6 ksi
@Temperature 302 °F		ISO 6721
 0.627 GPa
@Temperature 140 °C		90.9 ksi
@Temperature 284 °F		ISO 6721
 0.662 GPa
@Temperature 130 °C		96.0 ksi
@Temperature 266 °F		ISO 6721
 0.696 GPa
@Temperature 120 °C		101 ksi
@Temperature 248 °F		ISO 6721
 0.732 GPa
@Temperature 110 °C		106 ksi
@Temperature 230 °F		ISO 6721
 0.772 GPa
@Temperature 100 °C		112 ksi
@Temperature 212 °F		ISO 6721
 0.822 GPa
@Temperature 90.0 °C		119 ksi
@Temperature 194 °F		ISO 6721
 0.893 GPa
@Temperature 80.0 °C		130 ksi
@Temperature 176 °F		ISO 6721
 1.00 GPa
@Temperature 70.0 °C		145 ksi
@Temperature 158 °F		ISO 6721
 1.17 GPa
@Temperature 60.0 °C		170 ksi
@Temperature 140 °F		ISO 6721
 1.44 GPa
@Temperature 50.0 °C		209 ksi
@Temperature 122 °F		ISO 6721
 1.71 GPa
@Temperature 40.0 °C		248 ksi
@Temperature 104 °F		ISO 6721
 1.89 GPa
@Temperature 30.0 °C		274 ksi
@Temperature 86.0 °F		ISO 6721
 1.94 GPa
@Temperature 20.0 °C		281 ksi
@Temperature 68.0 °F		ISO 6721
 1.98 GPa
@Temperature 10.0 °C		287 ksi
@Temperature 50.0 °F		ISO 6721
 2.02 GPa
@Temperature 0.000 °C		293 ksi
@Temperature 32.0 °F		ISO 6721
 2.05 GPa
@Temperature -10.0 °C		297 ksi
@Temperature 14.0 °F		ISO 6721
 2.09 GPa
@Temperature -20.0 °C		303 ksi
@Temperature -4.00 °F		ISO 6721
 2.12 GPa
@Temperature -30.0 °C		307 ksi
@Temperature -22.0 °F		ISO 6721
 2.16 GPa
@Temperature -40.0 °C		313 ksi
@Temperature -40.0 °F		ISO 6721
 2.21 GPa
@Temperature -50.0 °C		321 ksi
@Temperature -58.0 °F		ISO 6721
Izod Impact, Notched  1.01 J/cm
@Temperature -40.0 °C		1.89 ft-lb/in
@Temperature -40.0 °F		ASTM D256
 1.12 J/cm
@Temperature 23.0 °C		2.10 ft-lb/in
@Temperature 73.4 °F		ASTM D256
Izod Impact, Unnotched  9.98 J/cm
@Temperature 23.0 °C		18.7 ft-lb/in
@Temperature 73.4 °F		ASTM D4812
 11.2 J/cm
@Temperature -40.0 °C		21.0 ft-lb/in
@Temperature -40.0 °F		ASTM D4812
Izod Impact, Notched (ISO)  10.0 kJ/m²
@Temperature -40.0 °C		4.76 ft-lb/in²
@Temperature -40.0 °F		ISO 180/1A
 10.0 kJ/m²
@Temperature -30.0 °C		4.76 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1A
 11.0 kJ/m²
@Temperature 23.0 °C		5.23 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Izod Impact, Unnotched (ISO)  55.0 kJ/m²
@Temperature -40.0 °C		26.2 ft-lb/in²
@Temperature -40.0 °F		ISO 180/1U
 55.0 kJ/m²
@Temperature -30.0 °C		26.2 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1U
 60.0 kJ/m²
@Temperature 23.0 °C		28.6 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched  7.00 J/cm²
@Temperature 23.0 °C		33.3 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
 7.50 J/cm²
@Temperature -40.0 °C		35.7 ft-lb/in²
@Temperature -40.0 °F		ISO 179/1eU
 7.50 J/cm²
@Temperature -30.0 °C		35.7 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
Charpy Impact, Notched  1.00 J/cm²
@Temperature -40.0 °C		4.76 ft-lb/in²
@Temperature -40.0 °F		ISO 179/1eA
 1.10 J/cm²
@Temperature -30.0 °C		5.23 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 1.10 J/cm²
@Temperature 23.0 °C		5.23 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
Tensile Creep Modulus, 1 hour 9000 MPa
@Temperature 23.0 °C		1.31e+6 psi
@Temperature 73.4 °F		ISO 899
 3330 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		483000 psi
@Temperature 73.4 °F,
Time 10000 hour		80MPa; ISO 899
 4070 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		590000 psi
@Temperature 73.4 °F,
Time 10000 hour		70MPa; ISO 899
 4260 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		618000 psi
@Temperature 73.4 °F,
Time 1000 hour		80MPa; ISO 899
 4550 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		660000 psi
@Temperature 73.4 °F,
Time 10000 hour		60MPa; ISO 899
 4860 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		705000 psi
@Temperature 73.4 °F,
Time 1000 hour		70MPa; ISO 899
 4900 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		711000 psi
@Temperature 73.4 °F,
Time 10000 hour		50MPa; ISO 899
 5190 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		753000 psi
@Temperature 73.4 °F,
Time 10000 hour		40MPa; ISO 899
 5230 MPa
@Temperature 23.0 °C,
Time 360000 sec		759000 psi
@Temperature 73.4 °F,
Time 100 hour		80MPa; ISO 899
 5310 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		770000 psi
@Temperature 73.4 °F,
Time 1000 hour		60MPa; ISO 899
 5420 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		786000 psi
@Temperature 73.4 °F,
Time 10000 hour		30MPa; ISO 899
 5590 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		811000 psi
@Temperature 73.4 °F,
Time 10000 hour		20MPa; ISO 899
 5620 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		815000 psi
@Temperature 73.4 °F,
Time 1000 hour		50MPa; ISO 899
 5690 MPa
@Temperature 23.0 °C,
Time 360000 sec		825000 psi
@Temperature 73.4 °F,
Time 100 hour		70MPa; ISO 899
 5710 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		828000 psi
@Temperature 73.4 °F,
Time 10000 hour		10MPa; ISO 899
 5860 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		850000 psi
@Temperature 73.4 °F,
Time 1000 hour		40MPa; ISO 899
 6050 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		877000 psi
@Temperature 73.4 °F,
Time 1000 hour		30MPa; ISO 899
 6100 MPa
@Temperature 23.0 °C,
Time 360000 sec		885000 psi
@Temperature 73.4 °F,
Time 100 hour		60MPa; ISO 899
 6190 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		898000 psi
@Temperature 73.4 °F,
Time 1000 hour		20MPa; ISO 899
 6200 MPa
@Temperature 23.0 °C,
Time 36000 sec		899000 psi
@Temperature 73.4 °F,
Time 10.0 hour		80MPa; ISO 899
 6290 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		912000 psi
@Temperature 73.4 °F,
Time 1000 hour		10MPa; ISO 899
 6400 MPa
@Temperature 23.0 °C,
Time 360000 sec		928000 psi
@Temperature 73.4 °F,
Time 100 hour		50MPa; ISO 899
 6600 MPa
@Temperature 23.0 °C,
Time 36000 sec		957000 psi
@Temperature 73.4 °F,
Time 10.0 hour		70MPa; ISO 899
 6630 MPa
@Temperature 23.0 °C,
Time 360000 sec		962000 psi
@Temperature 73.4 °F,
Time 100 hour		40MPa; ISO 899
 6800 MPa
@Temperature 23.0 °C,
Time 360000 sec		986000 psi
@Temperature 73.4 °F,
Time 100 hour		30MPa; ISO 899
 6920 MPa
@Temperature 23.0 °C,
Time 360000 sec		1.00e+6 psi
@Temperature 73.4 °F,
Time 100 hour		20MPa; ISO 899
 7030 MPa
@Temperature 23.0 °C,
Time 36000 sec		1.02e+6 psi
@Temperature 73.4 °F,
Time 10.0 hour		60MPa; ISO 899
 7040 MPa
@Temperature 23.0 °C,
Time 360000 sec		1.02e+6 psi
@Temperature 73.4 °F,
Time 100 hour		10MPa; ISO 899
 7270 MPa
@Temperature 23.0 °C,
Time 3600 sec		1.05e+6 psi
@Temperature 73.4 °F,
Time 1.00 hour		80MPa; ISO 899
 7330 MPa
@Temperature 23.0 °C,
Time 36000 sec		1.06e+6 psi
@Temperature 73.4 °F,
Time 10.0 hour		50MPa; ISO 899
 7520 MPa
@Temperature 23.0 °C,
Time 3600 sec		1.09e+6 psi
@Temperature 73.4 °F,
Time 1.00 hour		70MPa; ISO 899
 7580 MPa
@Temperature 23.0 °C,
Time 36000 sec		1.10e+6 psi
@Temperature 73.4 °F,
Time 10.0 hour		40MPa; ISO 899
 7730 MPa
@Temperature 23.0 °C,
Time 36000 sec		1.12e+6 psi
@Temperature 73.4 °F,
Time 10.0 hour		30MPa; ISO 899
 7810 MPa
@Temperature 23.0 °C,
Time 3600 sec		1.13e+6 psi
@Temperature 73.4 °F,
Time 1.00 hour		60MPa; ISO 899
 7870 MPa
@Temperature 23.0 °C,
Time 36000 sec		1.14e+6 psi
@Temperature 73.4 °F,
Time 10.0 hour		20MPa; ISO 899
 7940 MPa
@Temperature 23.0 °C,
Time 36000 sec		1.15e+6 psi
@Temperature 73.4 °F,
Time 10.0 hour		10MPa; ISO 899
 8120 MPa
@Temperature 23.0 °C,
Time 3600 sec		1.18e+6 psi
@Temperature 73.4 °F,
Time 1.00 hour		50MPa; ISO 899
 8390 MPa
@Temperature 23.0 °C,
Time 3600 sec		1.22e+6 psi
@Temperature 73.4 °F,
Time 1.00 hour		40MPa; ISO 899
 8550 MPa
@Temperature 23.0 °C,
Time 3600 sec		1.24e+6 psi
@Temperature 73.4 °F,
Time 1.00 hour		30MPa; ISO 899
 8660 MPa
@Temperature 23.0 °C,
Time 3600 sec		1.26e+6 psi
@Temperature 73.4 °F,
Time 1.00 hour		20MPa; ISO 899
 8700 MPa
@Temperature 23.0 °C,
Time 3600 sec		1.26e+6 psi
@Temperature 73.4 °F,
Time 1.00 hour		10MPa; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.126 %,
Temperature 23.0 °C		1450 psi
@Strain 0.126 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.115 %,
Temperature 23.0 °C		1450 psi
@Strain 0.115 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.231 %,
Temperature 23.0 °C		2900 psi
@Strain 0.231 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.254 %,
Temperature 23.0 °C		2900 psi
@Strain 0.254 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.388 %,
Temperature 23.0 °C		4350 psi
@Strain 0.388 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.351 %,
Temperature 23.0 °C		4350 psi
@Strain 0.351 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.477 %,
Temperature 23.0 °C		5800 psi
@Strain 0.477 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.528 %,
Temperature 23.0 °C		5800 psi
@Strain 0.528 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.682 %,
Temperature 23.0 °C		7250 psi
@Strain 0.682 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.616 %,
Temperature 23.0 °C		7250 psi
@Strain 0.616 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 60.0 MPa
@Strain 0.768 %,
Temperature 23.0 °C		8700 psi
@Strain 0.768 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 60.0 MPa
@Strain 0.854 %,
Temperature 23.0 °C		8700 psi
@Strain 0.854 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.06 %,
Temperature 23.0 °C		10200 psi
@Strain 1.06 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 70.0 MPa
@Strain 0.931 %,
Temperature 23.0 °C		10200 psi
@Strain 0.931 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 80.0 MPa
@Strain 1.10 %,
Temperature 23.0 °C		11600 psi
@Strain 1.10 %,
Temperature 73.4 °F		1h; Break; Isochronous; ISO 899
 80.0 MPa
@Strain 1.29 %,
Temperature 23.0 °C		11600 psi
@Strain 1.29 %,
Temperature 73.4 °F		10h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 6600 MPa
@Temperature 23.0 °C		957000 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.159 %,
Temperature 23.0 °C		1450 psi
@Strain 0.159 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.142 %,
Temperature 23.0 °C		1450 psi
@Strain 0.142 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.175 %,
Temperature 23.0 °C		1450 psi
@Strain 0.175 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.358 %,
Temperature 23.0 °C		2900 psi
@Strain 0.358 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.289 %,
Temperature 23.0 °C		2900 psi
@Strain 0.289 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.323 %,
Temperature 23.0 °C		2900 psi
@Strain 0.323 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.496 %,
Temperature 23.0 °C		4350 psi
@Strain 0.496 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.441 %,
Temperature 23.0 °C		4350 psi
@Strain 0.441 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.554 %,
Temperature 23.0 °C		4350 psi
@Strain 0.554 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.770 %,
Temperature 23.0 °C		5800 psi
@Strain 0.770 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.603 %,
Temperature 23.0 °C		5800 psi
@Strain 0.603 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.683 %,
Temperature 23.0 °C		5800 psi
@Strain 0.683 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.889 %,
Temperature 23.0 °C		7250 psi
@Strain 0.889 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.02 %,
Temperature 23.0 °C		7250 psi
@Strain 1.02 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.781 %,
Temperature 23.0 °C		7250 psi
@Strain 0.781 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 60.0 MPa
@Strain 0.984 %,
Temperature 23.0 °C		8700 psi
@Strain 0.984 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.32 %,
Temperature 23.0 °C		8700 psi
@Strain 1.32 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.13 %,
Temperature 23.0 °C		8700 psi
@Strain 1.13 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.44 %,
Temperature 23.0 °C		10200 psi
@Strain 1.44 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.72 %,
Temperature 23.0 °C		10200 psi
@Strain 1.72 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.23 %,
Temperature 23.0 °C		10200 psi
@Strain 1.23 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 80.0 MPa
@Strain 1.53 %,
Temperature 23.0 °C		11600 psi
@Strain 1.53 %,
Temperature 73.4 °F		100h; Break; Isochronous; ISO 899
 80.0 MPa
@Strain 1.88 %,
Temperature 23.0 °C		11600 psi
@Strain 1.88 %,
Temperature 73.4 °F		1000h; Break; Isochronous; ISO 899
 80.0 MPa
@Strain 2.40 %,
Temperature 23.0 °C		11600 psi
@Strain 2.40 %,
Temperature 73.4 °F		10000h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
 1.00e+16 ohm-cm
@Temperature 23.0 °C		1.00e+16 ohm-cm
@Temperature 73.4 °F		ASTM D257
Surface Resistance  >= 1.00e+15 ohm
@Temperature 23.0 °C		>= 1.00e+15 ohm
@Temperature 73.4 °F		ASTM D257
 >= 1.00e+15 ohm
@Temperature 23.0 °C		>= 1.00e+15 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.8
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.8
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 3.8
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.8
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 4.0
@Frequency 1000 Hz,
Temperature 23.0 °C		4.0
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 4.4
@Frequency 100 Hz,
Temperature 23.0 °C		4.4
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength  17.0 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		432 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		Short Time; ASTM D149
 23.0 kV/mm
@Thickness 1.60 mm,
Temperature 23.0 °C		584 kV/in
@Thickness 0.0630 in,
Temperature 73.4 °F		Short Time; ASTM D149
 31.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		787 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		IEC 60243-1
 17.0 kV/mm
@Thickness 2.00 mm,
Time 20.0 sec		432 kV/in
@Thickness 0.0787 in,
Time 0.00556 hour		IEC 60243-1
Dissipation Factor  0.0020
@Frequency 1000 Hz,
Temperature 23.0 °C		0.0020
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 0.0025
@Frequency 100 Hz,
Temperature 23.0 °C		0.0025
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.018
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.018
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 0.018
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.018
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index  400 V
@Temperature 23.0 °C		400 V
@Temperature 73.4 °F		UL 746A
 450 V
@Temperature 23.0 °C		450 V
@Temperature 73.4 °F		IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  90.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		50.0 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 90.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		50.0 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
Melting Point 225 °C437 °FASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 220 °C428 °FISO 75-1/-2
 220 °C428 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 205 °C401 °FISO 75-1/-2
 205 °C401 °FASTM D648
Deflection Temperature at 5.0 MPa 179 °C354 °F4x100x100mm plaque; ISO 75-1/-2
Deflection Temperature at 8.0 MPa 134 °C273 °FISO 75-1/-2
UL RTI, Electrical  130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
UL RTI, Mechanical with Impact  130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
UL RTI, Mechanical without Impact  130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
Flammability, UL94  HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
 HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		UL94
Oxygen Index 19 %19 %ASTM D2863
 19 %19 %ISO 4589-1/-2
Glow Wire Test  725 °C
@Thickness 1.50 mm		1340 °F
@Thickness 0.0591 in		IEC 60695-2-12
 725 °C
@Thickness 0.750 mm		1340 °F
@Thickness 0.0295 in		IEC 60695-2-12
 750 °C
@Thickness 0.750 mm		1380 °F
@Thickness 0.0295 in		Ignition; IEC 60695-2-13
 750 °C
@Thickness 1.50 mm		1380 °F
@Thickness 0.0591 in		Ignition; IEC 60695-2-13
 800 °C
@Thickness 3.00 mm		1470 °F
@Thickness 0.118 in		Ignition; IEC 60695-2-13
 825 °C
@Thickness 3.00 mm		1520 °F
@Thickness 0.118 in		IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AdditiveLubricant
AppearanceNatural Color
Drying RecommendedYes
FeaturesChemical Resistance, Good
 Dimensional Stability, Good
 Lubricated
 Moisture Absorption, Low
 Processability, Good
 Stiffness, Good
 Strength, Good
FillerGlass fiber reinforcement
FormsPellets
GenericPBT
Material StatusCurrent
Part Marking Code>PBT-GF30<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
Region Available - GlobalYes
Resin IdentificationPBT-GF30ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAutomotive Applications
 General Purpose
 Industrial Applications
 Parts, Engineering
 Parts, Machine/Mechanical
 Structural Parts

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38078.html

免责声明: 本文 DuPont Performance Polymers Crastin® SK605 NC010 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4