- 熔体流动速率 [g/10min]: 26.0
- 密度 [g/cm3]: 1.19
- 缺口冲击强度: 4.27
- 拉伸强度 [MPa]: 54.5
- 断裂伸长率 [%]: 73.8
- 弯曲模量 [MPa]: 2.24
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 | ||
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | ASTM D955 | ||
| Melt Flow | 26 g/10 min @Load 5.00 kg, Temperature 260 °C | 26 g/10 min @Load 11.0 lb, Temperature 500 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 54.5 MPa | 7900 psi | ASTM D638 | ||
| 55.0 MPa | 7980 psi | ISO 527-2 | |||
| Tensile Modulus | 2.03 GPa | 295 ksi | ASTM D638 | ||
| 2.10 GPa | 305 ksi | ISO 527-2 | |||
| Flexural Strength | 75.2 MPa | 10900 psi | ISO 178 | ||
| Flexural Yield Strength | 73.8 MPa | 10700 psi | ASTM D790 | ||
| Flexural Modulus | 2.24 GPa | 325 ksi | ASTM D790 | ||
| 2.35 GPa | 341 ksi | ISO 178 | |||
| Izod Impact, Notched | 4.27 J/cm @Temperature -40.0 °C | 8.00 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| 7.47 J/cm @Temperature 22.8 °C | 14.0 ft-lb/in @Temperature 73.0 °F | ASTM D256 | |||
| Izod Impact, Notched (ISO) | 35.7 kJ/m² @Temperature -40.0 °C | 17.0 ft-lb/in² @Temperature -40.0 °F | ISO 180 | ||
| 60.9 kJ/m² @Temperature 22.8 °C | 29.0 ft-lb/in² @Temperature 73.0 °F | ISO 180 | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | Unannealed; ASTM D648 | ||
| 103 °C | 217 °F | Unannealed; ISO 75-2/A | |||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 238 - 266 °C | 460 - 510 °F | |||
| Middle Barrel Temperature | 243 - 271 °C | 470 - 520 °F | |||
| Front Barrel Temperature | 249 - 277 °C | 480 - 530 °F | |||
| Nozzle Temperature | 254 - 271 °C | 490 - 520 °F | |||
| Melt Temperature | 254 - 271 °C | 490 - 520 °F | |||
| Mold Temperature | 54.4 - 82.2 °C | 130 - 180 °F | |||
| Drying Temperature | 110 °C @Time 14400 - 18000 sec | 230 °F @Time 4.00 - 5.00 hour | |||
| Dry Time | <= 12.0 hour | <= 12.0 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | Suggested Maximum | ||
| Shot Size | 50 - 80 % | 50 - 80 % | |||
| Screw Speed | 50 - 80 rpm | 50 - 80 rpm | |||
| Descriptive Properties | |||||
| Injection Rate | Moderate | ||||
| Melt-Volume Flow Rate, 260°C/5.0 kg (in3/10 min) | 1.34 | ISO 1133 | |||